LATI Latamid 66 H2 G/30 PA66 | GF30

Material attribute: ·Heat stabilized ·30% glass fiber reinforced

Package: 25KG/Bag

Get Quotation

LATI Latamid 66 H2 G/30 PA66 pellet Description

Latamid 66 H2 G/30 is a polyamide 66 resin manufactured by Lati Industrial Termoplastici S.p.A. This material contains 30% glass fiber (GF30 PA66 material), offering exceptional high-temperature resistance, good mechanical properties, and high strength.

LATI Latamid 66 H2 G/30 PA66 Advantage

GF30 PA66 material. Latamid 66 H2 G/30 contains 30% glass fiber reinforcement, offering higher strength, stiffness, and heat resistance compared to conventional polyamide materials.
Exceptional heat resistance. Compared to unreinforced polyamide, Lati 66 H2 G/30 GF30 PA66 material exhibits superior heat resistance. Its heat deflection temperature reaches260°C under 0.45MPa testing conditions and maintains 245°C even at 1.81MPa. Designed for long-term operation at 130°C, it is ideal for mechanical components and home appliance parts demanding high temperature resistance.

Why choose Baiyou as LATI Latamid 66 H2 G/30 PA66 pellets supplier?

Leading 30% glass fiber nylon 66 resin supplier (GF30 PA66 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

LATI Latamid 66 H2 G/30 PA66
Product information
Manufacturer		LATI industrial termoplastici S.p.A
Part Marking Code		>PA66 material<
Color		Natural color
Material Shape		PA66 Pellets
Features		·30% glass fiber reinforced ·High rigidity
Physical properties	Standard	Value	Unit
Density	ISO 1183	1.36	g/cm³
Linear shrinkage at moulding longitudinal 2.0mm/60MPa	ISO 294-4	0.35-0.65	%
Linear shrinkage at moulding transversal 2.0mm/60MPa	ISO 294-4	0.75-1.05	%
Moisture absorption in air after 24 hours	ISO 62-4	0.27	%
Dimensional stability		45
Mechanical behavior	Standard	Value	Unit
Tensile Modulus 1% Secant	ASTM D638	1200	Mpa
Tensile Strength Yield	ASTM D638	27	Mpa
Elongation Break	ASTM D638	700	%
Flexural Modulus	ISO 178	1100	Mpa
Charpy impact strength, unnotched at 23℃	ISO 179-1eU	85	kJ/㎡
Charpy impact strength, notched at 23℃	ISO 179-1eA	10	kJ/㎡
Tensile elongation at break (5mm/min), 23℃	ISO 527	3.2	%
Tensile elongation at break (5mm/min), 60℃	ISO 527	4.0	%
Tensile elongation at break (5mm/min), 90℃	ISO 527	5.5	%
Tensile elongation at break (5mm/min), 120℃	ISO 527	6.0	%
Tensile elongation at break (5mm/min), 150℃	ISO 527	6.5	%
Tensile strength at break (5mm/min), 23℃	ISO 527	175	MPa
Tensile strength at break (5mm/min), 23℃	ISO 527	175	MPa
Tensile strength at break (5mm/min), 60℃	ISO 527	135	MPa
Tensile strength at break (5mm/min), 90℃	ISO 527	110	MPa
Tensile strength at break (5mm/min), 120℃	ISO 527	100	MPa
Tensile strength at break (5mm/min), 150℃	ISO 527	85	MPa
Elastic modulus tensile (speed 1 mm/min), at 23℃	ISO 527	9400	MPa
Elastic modulus tensile (speed 1 mm/min), at 60℃	ISO 527	8500	MPa
Elastic modulus tensile (speed 1 mm/min), at 90℃	ISO 527	7400	MPa
Elastic modulus tensile (speed 1 mm/min), at 120℃	ISO 527	5500	MPa
Elastic modulus tensile (speed 1 mm/min), at 150℃	ISO 527	4400	MPa
Thermal	Standard	Value	Unit
Vicat Softening Temperature 50 N (heating rate 50℃/h)	ISO 306	255	°C
Coefficient of linear thermal expansion (CLTE) +30℃ to +100℃ (longitudinal)	ISO 11359-2	8	μm(m·℃)
Heat deflection temperature (HDT) 0.45MPa	ISO 75	260	℃
Heat deflection temperature (HDT) 1.8MPa	ISO 75	260	℃
C.U.T continuous use temperature long period (20,000H)		130	℃

⚠️The technical data sheet (TDS) of LATI Latamid H2 G/30 nylon 66 resin (PA66 material) from LATI Industria Termoplastici S.p.A., if there are differences, please refer to the official website of Lati.