Celanese Crastin SK605 PBT | GF30

 Celanese Crastin SK605 PBT pellet Description 

Celanese Crastin SK605 PBT Advantage

• GF30 PBT material, Celaense SK605 PBT material contains 30% glass fiber reinforcement (GF30 PBT material), providing superior high-temperature resistance, dimensional stability, rigidity, and strength compared to conventional polybutylene terephthalate.
• High-temperature resistance: Celasnese SK605 PBT achieves a heat deflection temperature of 205°C at 1.8 MPa without annealing, making it suitable for automotive components and electronic parts requiring high-temperature resistance.
• High Rigidity: Reinforced with 30% glass fiber, Celasnese SK605 PBT exhibits a modulus of elasticity of 9600 MPa at 23°C and 4.0 mm load. This provides exceptional rigidity and strength, making it suitable for manufacturing high-load-bearing components.

Why choose Baiyou as Celanese Crastin SK605 PBT pellets supplier?

• Leading 30% glass fiber reinforced Polybutylene terephthalate resin pellets supplier (GF30 PBTmaterial) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Celanese Crastin SK605 PBT
Product information
Manufacturer		Celanese corporation
Part Marking Code		>PBT material<
Color		Natural color
Material Shape		PBT Pellets
Features		·High strength ·30% glass fiber reinforced
Physical properties	Standard	Value	Unit
Density at 23℃	ISO 1183	1520	kg/m³
Emission of organic compounds at 23℃	VDA 277	90	μgC/g
Fogging at 23℃ F-value, refraction	ISO 6452	99	%
Odor at 23℃	VDA 270	3
Hardness	Standard	Value	Unit
Shore Hardness D	ASTM D2240	68
Mechanical behavior	Standard	Value	Unit
Flexural strength at 23℃, 4.0mm	ISO 178	200	MPa
Impact strength notced charpy at 23℃ 4.0mm	ISO 179/1eA2	10	kJ/㎡
Impact strength notced izod at 23℃ 4.0mm	ISO 180	9	kJ/㎡
Impact strength unnotced izod at 23℃ 4.0mm	ISO 179	65	kJ/㎡
Modulus of elasticity at 23℃, 4.0mm	ISO 527-2	9600	MPa
Tensile strain at break, 23℃ 4.0mm	ISO 527-2	2.5	%
Tensile strength at break, 23℃ 4.0mm	ISO 527-2	130	MPa
Thermal	Standard	Value	Unit
Heat deflection temperature (HDT), unannealed at 1.80 MPa	ISO 7502,02	205	°C
Melting point 10℃/min	ISO 11357-3	225	°C
UL RTI, Electrical 0.75 mm	UL 746	130	°C
UL RTI, Electrical 1.5 mm	UL 746	130	°C
UL RTI, Mechnical with impact 1.5 mm	UL 746	130	°C
UL RTI, Mechnical with impact 0.75 mm	UL 746	130	°C
UL RTI, Mechnical without impact 1.5 mm	UL 746	130	°C
UL RTI, Mechnical without impact 0.75 mm	UL 746	130	°C
Flammability	Standard	Value	Unit
Burning behavior at 23℃ 1.5mm	IEC 60695-11-10	HB
Burning behavior at 23℃ 0.75mm	IEC 60695-11-10	HB
Burning rate at 23℃, 1mm, FMVSS 302	ISO 3795	54	mm/min
Glow wire flammability index (GWFI) 3.0 mm	IEC 60695-2-12	825	°C
Glow wire flammability index (GWFI) 1.5 mm	IEC 60695-2-12	725	°C
Glow wire flammability index (GWFI) 0.75mm	IEC 60695-2-12	725	°C
Glow wire ignition temperature (GWIT) 0.75mm	IEC 60695-2-13	750	°C
Glow wire ignition temperature (GWIT) 1.5mm	IEC 60695-2-13	750	°C
Glow wire ignition temperature (GWIT) 3.0mm	IEC 60695-2-13	800	°C
Limiting oxygen index (LOI) at 23℃	ISO 4589-2	20	%
Processing guidelines	Standard	Value	Unit
Drying temperature		110-130	°C
Drying time		2-4	h
Melt temperature		240-260	°C
Moisuture content		0-0.04	%
Mold temperature		30-130	°C

⚠️The technical data sheet (TDS) of Celanese Crastin SK605 Polybutylene terephthalate resin (PBT material) from Celanese corporation, if there are differences, please refer to the official website of Celanese.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated