Formosa Tairirex HP825G HIPS

 Formosa Tairirex HP825G HIPS pellet Description 

Formosa Tairirex HP825G HIPS Advantage

• High impact resistant, Tairirex HP825G HIPS offers superior impact resistance compared to conventional polystyrene materials, achieving an Izod notch impact value of 88 J/m at 23°C and 6.4 mm test conditions. It is suitable for applications demanding high impact resistance, such as television housings and air conditioner casings.
• High gloss. Compared to other high-impact polystyrene materials in the Tairirex HP825  HIPS series, HP825G features a high gloss finish, making it suitable for consumer applications requiring an attractive appearance, such as washing machine housings.

Why choose Baiyou as Formosa Tairirex HP825G HIPS pellets supplier?

• Leading high impact polystyrene resin pellets supplier (HIPS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Formosa TAIRIREX HIPS HP825G
Product information
Manufacturer		Formosa Chemicals & Fibre Corporation
Part Marking Code		>HIPS material<
Process		Injection molding
Material Shape		HIPS Pellets
Flame Retardant		HB
Material Attribute		Injection grade
Specification		RoHS UL
Features		·High gloss· High tensile strength ·High heat distortion temperature ·Odorless ·General purpose grade ·Low monomer residue
Application		Appliance components A/C housing
UL File NO.		E162823
Physical properties	Standard	Value	Unit
Density 23°C	ISO 1183	1.04	g/cm³
Density 23°C	ASTM D792	1.04	g/cm³
Shrinkage 3.2mm	ASTM D955	0.4~0.7	%
Melt Index 200°C 5kg	ASTM D1238	3.5	g/10min
Melt Index 200°C 5kg	ISO 1133	3.5	g/10min
Residual Monomer		500	ppm
Mechanical behavior	Standard	Value	Unit
Tensile Modulus 23°C	ASTM D638	19000	kg/cm²
Tensile Modulus 23°C	ISO 527	2200	MPa
Tensile Strength 23°C	ASTM D638	300	kg/cm²
Tensile Strength 23°C	ISO 527	33	MPa
Elongation 23°C	ASTM D638	40	%
Elongation 23°C	ISO 527	45	%
Flexural Strength 23°C	ASTM D790	550	kg/cm²
Flexural Strength 23°C	ISO 178	54	MPa
Flexural Modulus 23°C	ASTM D790	20000	kg/cm²
Flexural Modulus 23°C	ISO 178	1800	MPa
Izod Notch Impact 23°C 6.4mm	ASTM D256	11	kg-cm/cm
Izod Notch Impact 23°C 6.4mm	ISO 180	88	J/m
Thermal	Standard	Value	Unit
Heat deflection temperature (HDT) 3.2mm Annealed at 80°C for 2 hours	ASTM D648	93	°C
Heat deflection temperature (HDT) 3.2mm Annealed at 80°C for 2 hours	ISO 75	98	°C
Vicat SofteningTemperature Annealed 3.2mm at 80°C for 2 hours	ASTM D1525	104	°C
Vicat Softening Temperature Annealed 3.2mm at 80°C for 2 hours	ISO 306	104	°C
Flammability	Standard	Value	Unit
Flame Rating All Color 1.5mm	UL94	HB
Flame Rating All Color 3.0mm	UL94	HB
UL	Standard	Value	Unit
UL FlameRating ALL 1.5mm	UL94	HB
UL FlameRating ALL 3.0mm	UL94	HB
HWI ALL 1.5mm	UL 746A	4	PLC
HWI ALL 3.0mm	UL 746A	4	PLC
HWI ALL 1.5mm	UL 746A	1	PLC
HWI ALL 3.0mm	UL 746A	1	PLC
RTI Elec ALL 1.5mm	UL 746B	50	°C
RTI Elec ALL 3.0mm	UL 746B	50	°C
RTI Imp ALL 1.5mm	UL 746B	50	°C
RTI Imp ALL 3.0mm	UL 746B	50	°C
RTI Str ALL 1.5mm	UL 746B	50	°C
RTI Str ALL 3.0mm	UL 746B	50	°C
Comparative Tracking Index	IEC 60112	0	PLC
HVTR	UL 746A	2	PLC
Arc Resistance	ASTM D495	6	PLC

⚠️The technical data sheet (TDS) of Formosa Tairirex HP825G high impact polystyrene resin (HIPS material) from Formosa chemical & fiber corporation, if there are differences, please refer to the official website of Formosa.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated