KEPITAL F20-03 POM

Melt flow rate: 9 g/10min

Packing: 25KG/Bag

Process: Injection molding

Viscosity: Medium Viscosity

Get Quotation

KEP Kepital F20-03 POM pellet Description

Kepital F20-03 is an injection molding copolymer polyacetal reisn (POM-C material) produced by Korean Engineering Plastics. It has a melt index of 9g/10min, medium viscosity, and is easy to process, is suitable for injection molding.

Kepital F20-03 Natural, as shown in the image on the left, is milky white POM pellet with an approximately ellipsoidal shape. It is also available in black. Please contact us if you require a custom color.👉+86 15837933829

KEP kepital F20-03 POM pellet Advantage

Good processing properties, Kepital F20-03 acetal material has a melt index of 9g/10min and medium viscosity, suitable for injection molding processing, In addition, compared to KEPITAL F20-02 POM, this material contains release agent, which facilitates successful demolding of the product and improves production efficiency.
The cost advantage is obvious. Compared with the polyoxymethylene materials of the same level, Kepital F20-03 has a more obvious price advantage. Price-sensitive manufacturers can give priority to this material.

Why choose Baiyou as KEPITAL F20-03 POM pellets supplier?

Leading copolymer polyoxymethylene resin pellets supplier (POM material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

KEPITAL® POM F20-03
Product information
Manufacturer		Korea Engineering Plastics Co., Ltd
Other Certificates		RoHS MSDS
Part Marking Code		>POM material<
Material Shape		POM Pellets
Process		Injection molding POM material
Polymer		Copolymer
Viscosity		Medium viscosity
FR		HB
Material Attribute		Injection grade
Specification		RoHS UL
UL File NO.		E120354
Physical properties	Standard	Value	Unit
Density	ISO 1183	1.41	g/cm³
Shrinkage Flow 100x3mm	INTERNAL METHOD	2.0	%
Water Absorption 23°C 50RH	ISO 62	0.2	%
Melt Index	ISO 1133	9	g/10min
Mechanical behavior	Standard	Value	Unit
Tensile Modulus	ISO 527	2750	Mpa
Tensile Strength	ISO 527	65	Mpa
Elongation Yield	ISO 527	10	%
Elongation Break	ISO 527	32	%
Flexural Strength	ISO 178	87	Mpa
Flexural Modulus	ISO 178	2550	Mpa
Charpy Notch Impact 23°C	ISO 179	6.5	kJ/m²
Charpy Notch Impact -30°C	ISO 179	5.5	kJ/m²
Thermal	Standard	Value	Unit
HDT 1.8MPa	ISO 75	100	°C
Melting Temperature	ISO 11357	165	°C
CLE	ISO 11359	1.2E-4	cm/cm/°C
Electrical properties	Standard	Value	Unit
Volume Resistivity	IEC 60093	1E+14	Ω.cm
Surface Resistivity	IEC 60093	1E+16	Ω
Dielectric Strength	IEC 60243	19	KV/mm
Flammability	Standard	Value	Unit
Flame Rating All Color 0.75mm	UL94	HB
Flame Rating All Color 1.5mm	UL94	HB
Flame Rating All Color 3.0mm	UL94	HB
Flame Rating All Color 6.0mm	UL94	HB
Injection molding		Value	Unit
Dry Temperature		80~90	°C
Dry Time		3~4	hr
Water Content Control		≤0.1	%
Feeding Zone Temperature		60~80	°C
Zone1 Temperature		170~180	°C
Zone2 Temperature		180~190	°C
Zone3 Temperature		190~200	°C
Nozzle Temperature		180~210	°C
Cylinder Temperature		170~210	°C
Mould Temperature		60~80	°C
Screw Speed		150~200	mm/s
Back Pressure		20	bar