Mitsubishi Novaduran 5010G30 PBT | GF30
Material attribute: 30% glass fiber reinforced; Heat resistant
Package: 25KG/Bag
Applications: Automotive parts; E&E applications
Package: 25KG/Bag
Applications: Automotive parts; E&E applications
Mitsubishi Novaduran 5010G30 PBT pellet Description
Novaduran 5010G30 is a polybutylene terephthalate resin pellet (PBT material) manufactured by Mitsubishi Engineering Plastics Corporation. Containing 30% glass fiber reinforcement, it offers excellent high-temperature resistance, dimensional stability, and superior mechanical strength. It is commonly used in automotive, electrical, and electronic components.
Mitsubishi Novaduran 5010G30 PBT Advantage
- GF30 PBT material, Mitsubishi 5010G30 PBT material contains 30% glass fiber reinforcement, offering superior high-temperature resistance and mechanical strength compared to conventional PBT materials.
- High heat resistance.Polybutylene terephthalate (PBT) material inherently possesses excellent high-temperature resistance. Mitsubishi Novaduran 5010G30 PBT further enhances its temperature resistance with the reinforcement of GF30. At a test environment pressure of 0.45 MPa, the heat deflection temperature reaches 220°C and the melting temperature reaches 224°C, making it highly suitable for applications requiring strong temperature resistance, such as automotive engine components and electrical parts.
- Excellent mechanical properties. Mitsubishi 5010G30 PBT material exhibits high rigidity and impact resistance, with a flexural modulus of 9000 MPa and an unnotched Charpy impact strength of 59 kJ/m² at 23°C.
- Exceptional dimensional stability, Compared to other resin materials, Mitsubishi 5010G30 GF30 PBT exhibits a water absorption rate of only 0.07% at 23°C and molding shrinkage of just 1.2% at 2.0mm. Its strong dimensional stability makes it suitable for manufacturing precision components.
Why choose Baiyou as Mitsubishi Novaduran 5010G30 PBT pellets supplier?
- Leading Polybutylene terephthalate resin pellets supplier (PBT material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
- Fastest Arrival, with warehouses in multiple ports
- 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
- Free Samples for production testing
- Wholesale price, even a piece of goods is based on the wholesale price
Key Attributes
| Mitsubishi Novaduran 5010G30 PBT | |||
| Product information | |||
| Manufacturer | Mitsubishi engineering plastic group | ||
| Part Marking Code | >PBT material< | ||
| Color | Natural color | ||
| Material Shape | PBT Pellets | ||
| Features | ·Glass fiber 30% filler | ||
| Application | ·Automotive application ·Electical & electronic applications ·Automotive electronics ·General purpose | ||
| Physical properties | Standard | Value | Unit |
| Density 23℃ | ISO 1183 | 1.53 | g/cm³ |
| Melt volume flow rate (MVR) (250℃ 5.0kg) | ISO 1133 | 40 | cm³/10min |
| Mold shrinkage across flow 2.0mm | Internal method | 1.2 | % |
| Mold shrinkage flow 2.0mm | Internal method | 0.4 | % |
| Water absorption (Saturation 23℃) | ISO 62 | 0.070 | % |
| Mechanical behavior | Standard | Value | Unit |
| Tensile modulus | ISO 527-1/1 | 9500 | MPa |
| Tensile stress (break) | ISO 527-1/1 | 140 | MPa |
| Tensile strain (break) | ISO 527-2/5 | 3.0 | % |
| Flexural Modulus | ISO 178 | 9000 | MPa |
| Flexural stress | ISO 178 | 215 | MPa |
| Charpy notched impact strength 23℃ | ISO 179 | 10 | kJ/㎡ |
| Charpy unnotched impact strength 23℃ | ISO 179 | 59 | kJ/㎡ |
| Thermal | Standard | Value | Unit |
| Deflection temperature (HDT) under load 0.45 MPa, annealed | ISO 75-2/B | ＞220 | °C |
| Deflection temperature (HDT) under load 1.8 MPa, annealed | ISO 75-2/B | 207 | °C |
| Melting temperature | ISO 11357-3 | 224 | °C |
| RTI Elec 0.8mm | UL 746B | 104 | °C |
| RTI Imp 0.8mm | UL 746B | 104 | °C |
| RTI Str 0.8mm | UL 746B | 104 | °C |
| Electrical | Standard | Value | Unit |
| Suface resistivity | IEC 60093 | 5.0E+16 | ohms |
| Volume resistivity | IEC 60093 | 2.0E+16 | ohms·cm |
| Electrical strength 1.0mm | IEC60243-1 | 27 | kV/mm |
| Electrical strength 2.0mm | IEC60243-1 | 24 | kV/mm |
| Dielectric constant (1MHz) | IEC 60250 | 3.5 | |
| Dielectric factor (1MHz) | IEC 60250 | 3.5 | |
| Comparative tracking index (CTI) | UL 746A | PLC 1 | |
| Flammability | Standard | Value | Unit |
| Flame rating 0.8mm | UL94 | HB | |
| Flame rating 1.5mm | UL94 | HB | |
| Flame rating 3.0mm | UL94 | HB | |
| Flame rating 6.0mm | UL94 | HB | |
| Injection molding guidance | Standard | Value | Unit |
| Drying temperature, hot air dryer | 120 | ℃ | |
| Drying time, hot air dryer | 5.0-8.0 | hr | |
| Rear temperature | 240 | ℃ | |
| Middle temperature | 245 | ℃ | |
| Front temperature | 255 | ℃ | |
Nozzle temperature | 255 | ℃ | |
| Mold temperature | 80-100 | ℃ | |
| Injection pressure | 20.0-150 | MPa | |
| Injection rate | moderate - fast | ||
| Screw speed | 80-120 | rpm | |
⚠️The technical data sheet (TDS) of Mitsubishi Novaduran 5010G30 PBT material from Mitsubishi engineering plastic group, if there are differences, please refer to the official website of Mitsubishi engineering plastic.
Partners
We have established long-term relationships with 80+ well-known companies around the world |
Warehouse And Shipping
20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China. |
Quantity (tonnes) | 1-100 | 100-300 | >300 |
Lead time (days) | 7-10 | 10-15 | To be negotiated |
Best Selling Product