Lanxess Envalior Pocan B3225 PBT | GF25

Material attribute: 25% glass fiber reinforced

Package: 25KG/Bag

Process: Injection molding

Get Quotation

Lanxess Envalior Pocan B3225 PBT pellet Description

Pocan B3225 is a polybutylene terephthalate (PBT) polymer manufactured by Envalior Engineering Materials Inc. This material contains 25% glass fiber reinforcement, hence it is also referred to as"GF25 PBT."It has a melt flow index of 20 g/10 min and is suitable for injection molding processes.

⚠️Envalior Engineering Materials Inc., an investment of Lanxess AG, utilizes Envalior for the production of B3325 GF25 PBT material at some of its facilities. The final packaging style of delivered goods may differ from the current image. For specific details, please contact our sales team.

Lanxess Envalior Pocan B3225 PBT Advantage

GF25 PBT, Lanxess B3225 PBT material contains 25% glass fiber, effectively enhancing the dimensional stability, heat resistance, and strength of the final product.

High-temperature resistance: Under a 0.45MPa test environment, Envalior B3225 PBT achieves a heat deflection temperature of 220°C, making it suitable for applications in relatively high-temperature environments.
High strength: Envalior GF25 PBT exhibits a tensile modulus of 7200 MPa, flexural modulus of 7000 MPa, and stress at break of 120 MPa, making it suitable for manufacturing load-bearing components.

Good processability, Lanxess B3225 GF25 PBT material exhibits a melt flow index (MFI or MVR) of 20 cm³/10 min at 260°C under a 2.16 kg test environment. Its high flow rate facilitates injection molding and is also suitable for producing thin-walled products.

Why choose Baiyou as Lanxess Envalior Pocan B3225 PBT pellets supplier?

Leading 25% glass fiber reinforced Polybutylene terephthalate resin pellets supplier (GF25 PBT material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Lanxess Envalior Pocan B3225 PBT
Product information
Manufacturer		Envalior engineering material Inc
Part Marking Code		>PBT material<
Color		Natural color
Material Shape		PBT Pellets
Process		Injection molding
Features		·25% glass fiber reinfoced
Physical properties	Standard	Value	Unit
Melt volume - flow rate (MVR) at 260℃ 2.16kg	ISO 1133	20	cm³/10min
Molding shrinkage (normal)	ISO 1133	1.4	%
Molding shrinkage (parallel)	ISO 1133	0.5	%
Water absorption	ISO 62	0.4	%
Humidity absorption	ISO 62	0.2	%
Density	ISO 1183	1450	kg/m³
Mechanical behavior	Standard	Value	Unit
Tensile Modulus	ISO 527	7200	MPa
Stress at break	ISO 527	120	MPa
Strain at break	ISO 527	3.4	%
Flexural Modulus	ISO 178	7000	MPa
Flexural strength	ISO 178	195	MPa
Flexural strain at flexural strength	ISO 178	4.1	%
Charpy impact strength 23℃	ISO 179/1eU	50	kJ/㎡
Charpy impact strength -30℃	ISO 179/1eU	45	kJ/㎡
Charpy notched impact strength 23℃	ISO 179/1eU	7.2	kJ/㎡
Charpy notched impact strength -30℃	ISO 179/1eU	7.1	kJ/㎡
Izod impact strength 23℃	ISO 180/1U	45	kJ/㎡
Izod impact strength -30℃	ISO 180/1U	40	kJ/㎡
Thermal	Standard	Value	Unit
Melt temperature (10℃/min)	ISO 11357	225	°C
Temp. of deflectin under load (1.8MPa)	ISO 75	205	°C
Temp. of deflectin under load (0.45MPa)	ISO 75	220	°C
Coeff. of linear therm. expansion (parallel)	ISO 11359	0.3	E-4/°C
Coeff. of linear therm. expansion (parallel)	ISO 11359	0.3	E-4/°C
Burning Behave. at 0.75mm nom. thicken	IEC 60695	HB
Burning Behave. at 1.5mm nom. thicken	IEC 60695	HB
Burning Behave. at 3.0mm nom. thicken	IEC 60695	HB
Oxygen index	ISO 4589	20	%
Glow wire flammability index GWFI	ISO 60695	2	mm
Electrical properties	Standard	Value	Unit
Relative permittivity (100Hz)	IEC 62631-2-1	3.8
Relative permittivity (1MHz)	IEC 62631-2-1	3.6
Dissipation factor (100Hz)	IEC 62631-2-1	15	E-4
Dissipation factor (1MHz)	IEC 62631-2-1	15	E-4
Volume resistivity	IEC 62631-2-1	＞1E13	Ohm*m
Surface resistivity	IEC 62631-2-1	＞1E15	Ohm
Comparative tracking index	IEC 60112	325	V
Electric strength	IEC 60243	30	kV/mm
Comparative tracking index (PLC)	UL746A	1
Process recommendation	Standard	Value	Unit
Drying temperature circulating air dryer		120	°C
Drying time circulating air dryer		4-8	h
Residual moisture content		0.00-0.02	%
Melt temperature (Tmin-Tmax)		250-270	°C
Mold temperature		80-100	°C

⚠️The technical data sheet (TDS) of Lanxess Envalior Pocan B3225 Polybutylene terephthalate polymer (PBT material) from Envailor engineering material Inc, if there are differences, please refer to the official website of Envalior.