Mitsubishi iupital f20-03 pom pellets

Mitsubishi Iupital F20-03 POM-C

Application: Auto parts, Transmission parts, Home appliance parts

Density: 1.41 g/cm³

Packing: 25KG/Bag
Get Quotation

 Mitsubishi Iupital F20-03 POM-C pellet 

Application

Mitsubishi Iupital F20-03 is a general-purpose copolymer polyoxymethylene resin material suitable for extrusion molding. It has medium viscosity and is an excellent material for manufacturing automotive parts, widely used by automakers such as Ford, Chrysler and General Motors.

Mitsubishi Iupital F20-03 POM-C pellet Advantage

  • Excellent polyoxymethylene material for automobiles. Mitsubishi Iupital F20-03 is an excellent POM material for automobile parts manufacturing. This material has been certified and used by many automobile manufacturers, including but not limited to Ford, Chrysler, General Motors
  • Good processing performance, Iupital F20-03 acetal has suitable processing conditions, melt index 9g/10min at 190℃ 2.16kg test environment, medium flow rate, suitable for injection molding processing, can be used to produce general lubricating parts

Why choose Baiyou as Mitsubishi Iupital F20-03 POM-C pellets supplier ?

  • Leading POM resin pellets supplier (Polyoxymethylene) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
  • Fastest Arrival, with warehouses in multiple ports
  • 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
  • Free Samples for production testing
  • Wholesale price, even a piece of goods is based on the wholesale price
 Key Attributes 
Mitsubishi Iupital F20-03 POM-C
Product information
ManufacturerMitsubishi engineering plastic crop
Part Marking Code>POM material<
MaterialPOM pellets
Specification·UL 
ProcessInjection molding POM material
PolymerCopolymer
ViscosityMedium viscosity
FeaturesGeneral purpose grade POM
Applications
·E&E applications ·General purpose ·Automotive electronics ·Automotive applications
Automotive specifications
·Ford WSK-M4D635-A2 ·CHRYSLER MS-DB-100 CPN 1586 Color: Black
·CHRYSLER MS-DB-100 CPN1532 Color: Natural color ·GM GMP.POM.005 Color:Black
·GM GMP.POM .005 Color: Natural ·GM GMW22P-POM-C2
Physical properties  StandardValueUnit
DensityISO 11831.41g/cm³
Shrinkage flow 3.0mmInternal method2.0%
Water absorption 23℃ 60RHInternal method0.22%
Melt index 190℃ 2.16kgISO 11339g/10min
Melt index 190℃ 2.16kgISO 11337.70cm³/10min
Mechanical behaviorStandardValueUnit
Tensile modulusISO 5272900MPa
Tensile Strength yieldISO 52764.0Mpa
Elongation yeildISO 5278.5%
Elongation breakISO 52735%
Flexural Strength 2.0mm/minISO 17890Mpa
Flexural Modulus 2.0mm/minISO 1782600Mpa
Charpy Notch Impact 23℃ISO 1797.0kJ/m²
Charpy Un-Notch impact 23℃
ISO 179250kJ/m²
ThermalStandardValueUnit
HDT unannealed 0.45MPaISO 75156°C
HDT unannealed 1.8MPaISO 75100℃
Melt temperatureISO 11357166℃
CLE Flow ISO 113591.1E-4cm/cm/°C
CLE xFlow ISO 113591.1E-4cm/cm/°C
Electrical propertiesStandardValueUnit
Volume Resistivity IEC 60093 1E+14Ω.cm
Surface ResistivityIEC 600931E+16Ω
Dielectric Strength 1.0mmIEC 6024332KV/mm
Dielectric Strength 3.0mmIEC 6024319KV/mm
Dielectric constant 1MHzIEC 602503.9
Dielectric constant 100MHzIEC 602503.9
Dissipation factor 1MHzIEC 602500.007
Dissipation factor 100MHzIEC 602500.002
CTIIEC 60112600V
FlammabilityStandardValueUnit
Flame Rating All Color 0.75mm  UL94HB
Flame Rating All Color 1.5mmUL94HB
Flame Rating All Color 3.0mmUL94HB
Flame Rating All Color 6.0mmUL94HB
Injection moldingStandardValueUnit
Dry temperature80℃
Dry time3.0~4.0hr
Zone1 temperature170℃
Zone2 temperature180℃
Zone3 temperature190℃
Nozzle temperature180~210℃
Mould temperature60~80℃
Injection pressure50~100MPa
Injection speedmoderate
Screw speed80~120℃
⚠️The  technical data sheet of  Mitsubishi Iupital F20-03 POM from Mitsubishi engineering plastic company, if there are difference, please refer to the offical websit of  Mitsubishi
  Partners  
We have established long-term relationships with 80+ well-known  companies around the world
  Warehouse And Shipping  
20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.
Quantity (tonnes)
1-100
100-300
>300
Lead time (days)
7-10
10-15
To be negotiated