Wanhua Wanblend CA3250 PC/ABS

Material attribute: UL 94 V-0 flame retardant

Package: 25 KG/Bag

Process: Injection molding

Get Quotation

Wanhua Wanblend CA3250 PC/ABS Description

Wanblend CA3250 is a flame-retardant polycarbonate and acrylonitrile-butadiene-styrene (ABS) blend resin manufactured by Wanhua Chemical. Also known as “PC alloy material,” it has a melt flow index of 18 and is suitable for injection molding. It can be used in electronic and electrical equipment .

Wanblend CA3250 PC alloy Advantage

Flame retardant plastic, Wanblend CA3250 PC alloy features high-performance flame-retardant properties, achieving UL94 V-0 flame-retardant ratings at a thickness of 1.5 mm. It meets the requirements for general home appliance applications. Additionally, this material is halogen-free, complying with environmental standards while preventing corrosion of metal components in electronic products.
Good machinability. Wanblend CA3250 PC/ABS resin has a melt flow rate (MFR) of 18 g/10 min under test conditions of 260°C and 5 kg, indicating a moderate flow rate; it is suitable for use in the vast majority of injection molding machines.

Why choose Baiyou as Wanhua Wanblend CA3250 PC/ABS supplier?

Leading PC alloy resin supplier (PC/ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Wanhua Wanblend CA3250 PC/ABS
Product information
Manufacturer		Wanhua Chemical
Other Certificates		MSDS
Part Marking Code		>PC/ABS material<
Color		Natural color
Material Shape		PC alloy Pellets
Process		Injection molding
Features		·UL 94 V-0 Flame retardant
Additives		Mold release
Physical properties	Standard	Value	Unit
Relative Density （water=1）		1.1-1.25
Density	ASTM D792	1.18	g/cm³
Melt flow rate, MFR at 260℃ 5kg	ASTM D1238	21	cm³/10min
Mold shrinkage	ASTM D955	0.5-0.7	%
Auto-ignition temperature	ISO 62	0.15	%
Water absorption at 23℃, 24h	ASTM D570	0.5-0.7	%
Mechanical behavior	Standard	Value	Unit
Yield strain at 1 mm/min		4
Strain at break at 50 mm/min		100
Tensile modulus, 1 mm/min		2500	MPa
Stress, break, 50 mm/min	ASTM D638	60	MPa
Flexural strength, 2 mm/min	ASTM D790	90	MPa
Flexural modulus, 2 mm/min	ASTM D790	2700	MPa
Ball indentation hardness, H358 /30	ISO 2039-1	95	MPa
Impact	Standard	Value	Unit
Izod notched impact strength at 23℃	ASTM D256	650	kJ/㎡
Thermal	Standard	Value	Unit
Vicat Softening Temperature, rate B/50	ASTM D1525	103	°C
Heat Distortion Temperature at 1.8 MPa, 4.0mm	ASTM D648	83	℃
Aumo-ignition temperature		＞390	℃
Decompositon temperature		≥380	℃
Flash point		400	℃
Flame rating at 1.5 mm	UL 94	V-0
Electrical	Standard	Value	Unit
Volume resistivity	IEC 60093	10^14	Ω.m
Surface resistivity	IEC 60093	1^16	Ω
Injection molding guidance	Standard	Value	Unit
Melting piont		＞100	℃
Drying temperature		80	℃
Injection temperature		240-270	℃
Drying time		4-6	hrs