LG LUPOY GN5001RFH PC/ABS

Material attribute: ·Flame retardant ·UL 94 5VA ·Halogen free

Melt index: 12.8g/10min @ 250℃ 2.16kg

Get Quotation

LG LUPOY GN5001RFH PC/ABS Description

Lupoy GN5001RFH is a polycarbonate and acrylonitrile-butadiene-styrene (ABS) alloy resin manufactured by LG Chem, also known as"PC/ABS material."It meets the UL 94 5VA flame-retardant rating, is halogen-free, and is commonly used in automotive and home appliance components.

lupoy gn5001rfh flame retardant pc alloy resin

LUPOY GN5001RFH PC alloy resin is manufactured at multiple plants; we will give priority to products manufactured at the Guangzhou, China plant.

LUPOY GN5001RFH PC/ABS is available in a variety of colors, including natural, white, and black. The image on the left shows LUPOY GN5001 RFH WA384 high-gloss titanium white PC/ABS pellets, which are roughly cylindrical in shape.

If you would like a custom color, please contact us.

LG LUPOY GN5001RFH PC/ABS Advantage

Halogen free flame retardant, Lupoy GN5001RFH achieves high-efficiency UL 94 5VA flame retardancy at a test thickness of 2.5 mm and contains no halogen-based flame retardants. It is ideal for the processing of mechanical parts and electronic products and causes minimal corrosion to metals and connectors.

Why choose Baiyou as LG LUPOY GN5001RFH PC/ABS supplier?

Leading polycarbonate and Acrilonitrilo, butadieno y estireno Resina de aleación supplier (PC/ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

LG LUPOY GN5001RFH PC/ABS
Product information
Manufacturer		LG Chem
Other Certificates		MSDS
Part Marking Code		>PC/ABS material<
Color		·Natural color ·White ·Black
Material Shape		PC alloy Pellets
Process		Injection molding
Features		·UL 94 5VA ·Flame retardant ·Halogen free
Physical properties	Standard	Value	Unit
Specific gravity	ISO 1183	1190	kg/m³
Shrinkage , flow 2.0 mm	ISO 294	0.4-0.6	%
Shrinkage , xflow 2.0 mm	ISO 294	0.4-0.6	%
Water absorption 23℃, 50% RH	ISO 62	0.20	%
Rockwell hardness, R-Scale	ISO 2039	118
Mechanical behavior	Standard	Value	Unit
Tensile strength, yield 4.0 mm, 50 mm/min	ISO 527	60	MPa
Tensile strength, break 4.0 mm, 50 mm/min	ISO 527	56	MPa
Tensile elongation, yield, 4.0 mm 50 mm/min	ISO 527	4	%
Tensile elongation, break, 4.0 mm 50 mm/min	ISO 527	100	%
Tensile modulus,4 mm, 1mm/min	ISO 527	2570	MPa
Flexural strength, 4 mm, 2.0 mm/min	ISO 178	95	MPa
Flexural modulus, 4 mm, 2.0 mm/min	ISO 178	2360	MPa
Impact	Standard	Value	Unit
Izod impact strength , notched 4.0 mm 23℃	ISO 180	43	kJ/㎡
Izod impact strength , notched 4.0 mm -30℃	ISO 180	14	kJ/㎡
Izod impact strength , notched 4.0 mm -40℃	ISO 180	12	kJ/㎡
Charpy impact strength, notched 4.0 mm 23℃	ISO 179	45	kJ/㎡
Charpy impact strength, notched 4.0 mm -30℃	ISO 179	13	kJ/㎡
Charpy impact strength, notched 4.0 mm -40℃	ISO 179	12	kJ/㎡
Thermal	Standard	Value	Unit
Vicat Softening Temperature, 50N, 50℃/hr	ISO 306	106	°C
Coefficient of linear thermal expansion, flow	ISO 11359	72	10⁻⁶m/m·℃
Coefficient of linear thermal expansion, xflow	ISO 11359	79	10⁻⁶m/m·℃
Heat deflection temperature, 0.45 MPa, 4.0 mm flatwise unannealed	ISO 75	101	℃
Heat deflection temperature, 1.8 MPa, 4.0 mm flatwise unannealed	ISO 75	87	℃
Electrical	Standard	Value	Unit
Comparative tracking index (CTI), solution A	UL 746A	2	PLC
Dielectrics constant, 23 ℃	ASTM D150	2.8
Dielectrics strength, 23℃ 2.0 mm	ASTM D149	20	kV/mm
Flame retardant	Standard	Value	Unit
Flammability 2.5 mm	UL 94	5VA
Injection molding guidance	Standard	Value	Unit
Drying temperature		75-85	℃
Drying time		3-5	hrs
Maximum moisture content		0.04	%
Melt temperature		235-270	℃
Nozzle temperature		250-270	℃
Front - Zone 3 temperature		250-280	℃
Middle - Zone 2 temperature		240-260	℃
Rear- Zone 1 temperature		225-245	℃
Mold temperature		50-80	℃