Celanese Hostaform C 13021 POM

Material attribute: High flow

Package: 25 KG/Bag

Process: Injection molding

Get Quotation

Celanese Hostaform C 13021 POM Description

Hostaform C13021 is high flow copolymer acetal resin produced by (POM material),melt flow rate is 14, suitable for thin-walled and complex parts.

Celanese Hostaform C 13021 POM Advantage

High liquidity POM, Hostaform C13021 acetal resin has a melt volume rate of 12 cm³/10 min under test conditions of 190°C and 2.16 kg; compared to the more commonly used Hostaform C9021 POM resin, it offers higher flowability and is better suited for thin-walled and complex applications.

Why choose Baiyou as Celanese Hostaform C 13021 POM supplier?

Leading polyacetal resin supplier (PC material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Celanese Hostaform C 13021 POM
Product information
Manufacturer		Celanese company
Other Certificates		MSDS
Part Marking Code		>POM material<
Color		·Natural color ·Black
Material Shape		POM Pellets
Process		Injection molding
Features		·High flow
Additives		Release agent
Physical properties	Standard	Value	Unit
Density	ISO 1183	1410	kg/m³
Melt volume rate, MVR at 190℃/2.16 kg	ISO 1133	12	cm³/10min
Mold shrinkage, parallel	ISO 294-4	2	%
Mold shrinkage, normal	ISO 294-4	1.8	%
Humidity absorption	ISO 62	0.2	%
Water absorption	ISO 62	0.65	%
Mechanical behavior	Standard	Value	Unit
Tensile modulus	ISO 527	2900	MPa
Yield stress	ISO 527	65	MPa
Yield strain	ISO 527	9	%
Nominal strain at break	ISO 527	28	%
Tensile creep modulus,1 h	ISO 899-1	2500	MPa
Tensile creep modulus,1000 h	ISO 899-1	1300	MPa
Charpy impact strength, 23℃	ISO 179	200	kJ/㎡
Charpy impact strength, -30℃	ISO 179	200	kJ/㎡
Charpy notched impact strength, 23℃	ISO 179	6.5	kJ/㎡
Charpy notched impact strength, -30℃	ISO 179	6	kJ/㎡
Thermal	Standard	Value	Unit
Vicat Softening Temperature, rate B/50	ISO 306	140	°C
Vicat Softening Temperature, rate B/120	ISO 306	141	°C
Thermal conductivity	ISO 8302	0.2	W/m·℃
CTE, 23℃ to 80℃, xflow	ISO 11359-2	7.0E-05	1/℃
Ball pressure test, 125℃ +/- 2℃	IEC 60695-10-2	Passed
Melt temperature, 10 ℃ /min	ISO 11357-1/-3	166	℃
Temperature of deflection under load, 1.8 MPa	ISO 75	106	℃
Coefficient of linear thermal expansion, parallel	ISO 11359	110	E-6/K
Burning behavior at 1.5 mm nominal thickness 1.5 mm	IEC 60695	HB
Burning behavior at 1.5 mm nominal thickness 3.0 mm	IEC 60695	HB
Electrical	Standard	Value	Unit
Volume resistivity	IEC 62631-3-1	1E12	Ohm*m
Surface resistivity	IEC 62631-3-2	1E14	Ohm
Dissipation factor, 100 Hz	IEC 62631-2-1	20	E-4
Dissipation factor, 1 MHz	IEC 62631-2-1	50	E-4
Relative permittivity, 100 Hz	IEC 62631-3-1	4
Relative permittivity, 1 MHz	IEC 62631-3-1	4
Electric strength	IEC 60243-1	35	kV/mm
Comparative tracking index	IEC 60112	600