Celanese Hostaform S 9363 POM

 Celanese Hostaform S 9363 POM Description 

Hostaform S 9363 is manufactured at Celanese Corporation plant in the United States; standard colors include natural and black.

Hostaform S 9363 natural color is white POM; as shown in the image on the left, it consists of nearly spherical granules. Please contact us if you require a custom color.

Celanese Hostaform S 9363 POM Advantage

• Impact modified, Hostaform S 9363 POM resin has been impact-modified to provide excellent impact resistance, even in extreme low-temperature environments of -30°C, its flexibility is significantly better than that of conventional POM Hostaform C9021.

• Automotive application POM. Thanks to its outstanding properties, Hostaform S 9363 POM has received material certification from numerous automotive OEMs, including but not limited to Changan, Ford, General Motors, Li Auto, Renault, and Stellantis—Chrysler, and can be used with confidence in automotive applications.

Why choose Baiyou as Celanese Hostaform S 9363 POM supplier?

• Leading impact modified acetal resin supplier (POM material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Celanese Hostaform S 9363 POM
Product information
Manufacturer		Celanese Corporation
Other Certificates		MSDS
Part Marking Code		>POM-HI material<
Color		·Natural color ·Black
Material Shape		POM Pellets
Process		·Injection molding ·Extrusion
Features		·High impact resistance ·Low temperature resistance
Additives		Release agent
Automotives		·Changan MTS-F01-02-001-A3 ·Ford WSF-M4D618-A ·General Motors GMW22P-POM-C2P1 ·Li Auto Q/LiA5310020 ·Stellantis - Chrysler MS.50095/CPN-2726 CPN-2940
Physical properties	Standard	Value	Unit
Density	ISO 1183	1380	kg/m³
Melt volume rate, MVR at 190℃/2.16 kg	ISO 1133	5.5	cm³/10min
Mold shrinkage, parallel	ISO 294-4	1.8	%
Mold shrinkage, normal	ISO 294-4	1.8	%
Water absorption, 2 mm	ISO 62	0.8	%
Humidity absorption, 2 mm	ISO 62	0.25	%
Mechanical behavior	Standard	Value	Unit
Tensile stress, yield, 50 mm/min	ISO 527	50	MPa
Tensile strain, yield, 50 mm/min	ISO 527	12	%
Tensile modulus	ISO 527	2000	MPa
Flexural modulus	ISO 178	2000	MPa
Hardness, Rockwell, M-scale	ISO 2039	65	MPa
Poisson's ratio		0.41
Impact	Standard	Value	Unit
Izod impact impact strength 23℃	ISO 180/1A	13	kJ/㎡
Izod impact impact strength -30℃	ISO 180/1A	8	kJ/㎡
Izod impact impact strength -40℃	ISO 180/1A	N	kJ/㎡
Charpy impact strength 23℃	ISO 179/1eU	N	kJ/㎡
Charpy impact strength -30℃	ISO 179/1eU	N	kJ/㎡
Charpy notched impact strength 23℃	ISO 179/1eA	13	kJ/㎡
Charpy notched impact strength -30℃	ISO 179/1eA	8	kJ/㎡
Thermal	Standard	Value	Unit
Melting Temperature, 10℃/min	ISO 11357	165	°C
Coefficient of linear thermal expansion (CLTE), parallel	ISO 11359	110	E-6/K
Coefficient of linear thermal expansion (CLTE), normal	ISO 11359	110	E-6/K
Temperature of deflection under load, 1.8 MPa	ISO 75	84	℃
Temperature of deflection under load, 0.45 MPa	ISO 75	148	℃
Injection molding guidance	Standard	Value	Unit
Drying temperature		100	℃
Drying time		3-4	hrs
Maximum moisture content		0.2	%
Melt temperature		180-210	℃
Hopper temperature		60-80	℃
Mold temperature		60-70	℃
Hold pressure range		60-120	MPa
Hold pressure time		2h²-3	s
Back preesure		2	MPa
Ejection temperature		129	℃

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated

---

References and Notes

1. Celanese ,"Hostaform S 9363 copolymer acetal impact modified technical data sheet", Celanese, 03/11/2026