DOW Elite 5401G Enhanced PE

Application: Food packaing, packaging film

Melt flow rate: 1.0 g/10min

Density: 0.918 g/cm³

Packing: 25KG/Bag

Process: Extrusion molding / Blow molding

Get Quotation

DOW Elite 5401G enhanced polyethylene Description

Application

Elite 5401G is a linear low-density polyethylene material produced by Dow Chemical specifically for high-performance blown film. 5401G LDPE is often used as a packaging material due to its good sealing, tensile properties, puncture resistance and impact resistance.

DOW Elite 5401G enhanced polyethylene pellet Advantage

Plastic material for food and drug packaging. Elite 5401G complies with FDA, EU 10/2011 and Canadian HPFB food and drug contact certification and can be used for general food and drug packaging
Good processing performance. As a film-grade polyethylene material with excellent performance, ELITE 5401G has good processing conditions. At the same time, the addition of anti-blocking agent can effectively avoid adhesion during film production and storage.
Patented technology improves performance materials. ELITE 5401G uses Dow Chemical INSITE technology and metallocene catalysis to make polyethylene materials, making the finished product more flexible and with lower heat sealing temperature, which has great advantages in food and beverage automated packaging.

Company Profile

Baiyou is affiliated to Luoyang Dahao Industry & Trade Company Limited which is a large joint-stock company specializing in chemical raw materials, was established in2003, has 500+employees,20+years of plastic product manufacturing, chemical raw material import and export, and a registered capital of 15 million dollars.

Why choose Baiyou as DOW Elite 5401G enhanced polyethylene pellet supplier?

Leading EPE resin supplier (expandable polyethylene) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

DOW Elite 5401G Enhanced polyethylene
Product information
Manufacturer		The DOW chemical company
Part Marking Code		>enhanced polyethylene material<
Material Shape		EPE material Pellets
Process		Extrusion molding EPE material; Blow molding EPE material
Material Attribute		Film grade EPE pellet; Antiblock; Food contact grade EPE pellet
Specification		EU 10/2011; FAD FCN424; Canadian HPFB No. Objection(With limitations)
Features		Non processing aid; Good tear strength; High impact; Medium stiffness
Application		Automatci packaging; Food packaging fim; Packaging fim
Additives		Antiblock slip agent
Physical property	Standard	Value	Unit
Density	ASTM D1505	0.918	g/cm³
Density base resin	INTERNAL METHOD	0.917	g/cm³
Melt Index 190°C 2.16kg	ASTM D1238	1.0	g/10min
Thickness film	INTERNAL METHOD	25	μm
Mechanical behavior	Standard	Value	Unit
Tensile Modulus Flow Film	ASTM D882	70.3	J/cm³
Tensile Modulus xFlow Film	ASTM D882	66.2	J/cm³
Tensile Strength Film	ASTM D882	11.7	Mpa
Tensile Strength xFlow Film	ASTM D882	11.0	Mpa
Tensile Strength Flow Break Film	ASTM D882	33.8	Mpa
Tensile Strength xFlow Break Film	ASTM D882	27.6	Mpa
Elongation Flow Break	ASTM D882	400	%
Elongation xFlow Break	ASTM D882	450	%
Falling Weight Impact Strength	ASTM D1709	450	g
Elmendorf tear strength flow	ASTM D1922	250	g
Elmendorf tear strength xflow	ASTM D1922	550	g
Secant modulus 1% flow	ASTM D882	179	MPa
Secant modulus 2% flow	ASTM D882	159	MPa
Secant modulus 1% xflow	ASTM D882	200	MPa
Secant modulus 2% xflow	ASTM D882	165	MPa
Puncuture resistance energy film	INTERNAL METHOD	1.69	J
Puncuture resistance force film	INTERNAL METHOD	35.6	N
Puncuture resistance film	INTERNAL METHOD	9.10	J/cm³
Optical performance	Standard	Value	Unit
Gloss 45°	ASTM D2457	33
Haze	ASTM D1003	22.0	%
Thermal	Standard	Value	Unit
Vicat softening temperature	ASTM D1525	100	℃
Melting temperature DSC	INTERNAL METHOD	123	°C