LG LI911 ASA

 LG LI911 ASA pellet Description 

LG LI911 ASA Advantage

• Excellent weather resistance,  LG LI911 ASA material exhibits excellent UV resistance. Unlike ABS material, which tends to yellow after prolonged outdoor exposure, this material maintains its superior appearance even under intense UV radiation. It is suitable for automotive exterior trim, outdoor equipment housings, and outdoor electronic device enclosures where high aesthetic performance is required and long-term exposure to direct sunlight is anticipated.
• Good processability，LG LI911 resin exhibits a melt flow index (MFI or MVR) of 20g/10min under a 220°C, 10kg test environment. Its high flow properties make it suitable for producing thin-walled and complex parts, while its excellent processability allows direct application in ABS material processing equipment.

Why choose Baiyou as LG LI911 ASA pellets supplier?

• Leading Acrylonitrile-styrene-acrylate resin pellets supplier (ASA material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

LG LI911 ASA
Product information
Manufacturer		LG chemical Ltd.
Part Marking Code		>ASA material<
Material Shape		ASA Pellets
Process		Injection molding
Flame retardant		HB
Material attribute		·High flow ·Good weatherability
Application		·Air conditioner grill ·Sawing machine cover ·Electric/Electronic applications
Physical properties	Standard	Value	Unit
Specific Gravity	ASTM D792	1.07	g/cm³
Molding Shrinkage flow, 3.2mm	ASTM D955	0.4~0.7	%
Melt Index 220°C 10kg	ASTM D1238	20	g/10min
Hardness	Standard	Value	Unit
Rockwell hardness (R-scale)	ASTM D785	107
Mechanical behavior	Standard	Value	Unit
Tensile strength 3.2mm at yield, 50mm/min	ASTM D638	500	kg/c㎡
Tensile elongation 3.2mm at yield, 50mm/min	ASTM D638	＞6	%
Tensile elongation 3.2mm at break 50mm/min	ASTM D638	＞20	%
Flexural modulus 3.2mm 1mm/min	ASTM D638	22,100	kg/c㎡
Flexural strength 3.2mm 15mm/min	ASTM D790	800	kg/c㎡
Flexural modulus 3.2mm 15mm/min	ASTM D790	23,500	kg/c㎡
Izod impact strength, 6.4mm (notched) 23℃	ASTM D256	12	kg·cm/cm
Izod impact strength, 6.4mm (notched) -30℃	ASTM D256	3	kg·cm/cm
Izod impact strength, 3.2mm (notched) 23℃	ASTM D256	14	kg·cm/cm
Izod impact strength, 3.2mm (notched) -30℃	ASTM D256	3	kg·cm/cm
Impact strength notched izod 23℃ 6.4mm	ASTM D256	140	J/m
Thermal	Standard	Value	Unit
Heat deflection temperature, 6.4mm (Unannealed) 18.6kg	ASTM D648	87	°C
Heat deflection temperature, 6.4mm (Unannealed) 4.6kg	ASTM D648	96	°C
Vicat softening temperature rare A (50℃/h)50 N	ASTM D1525	96	°C
Flammability	Standard	Value	Unit
Flammability 0.8mm	UL94	HB
Flammability 1.6mm	UL94	HB
Flammability 2.5mm	UL94	HB
Flammability 3.2mm	UL94	HB
Injection molding guide	Standard	Value	Unit
Back pressure		5-10	kg/c㎡
Drying temperature		80-90	℃
Dry time		2-3	hrs
Melt temperature		200~230	℃
Middle cylinder temperature		220~240	℃
Moisture content(Max)		0.1	%
Cylinder temperature	Rear	180-200	℃
	Middle	190-210	℃
	Front	210-220	℃
Mold temperature		40~80	℃
Nozzle temperature		210~220	℃
Screw speed		50-100	rpm

⚠️The technical data sheet (TDS) of LG LG LI911 Acrylonitrile-styrene-acrylate resin (ASA material) from LG chemical, if there are differences, please refer to the official website of LG chemical.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated