Lotte INFINO WP-1069 PC/ABS

Material attribute: ·High flow

Package: 25 KG/Bag

Get Quotation

Lotte INFINO WP-1069 PC/ABS Description

INFINO WP-1069 is blended resin composed of polycarbonate and acrylonitrile-butadiene-styrene, manufactured by Lotte Chemical. It is also known as"PC/ABS material,"has a melt flow index of 47, and features high flowability. It is commonly used in the production of automotive and electronic products.

Lotte INFINO WP-1069 PC/ABS Advantage

High liquidity, Compared to conventional PC/ABS, INFINO WP-1069 PC/ABS resin has a melt flow index (MFI) of 47 g/10 min at 250°C and 10 kg, making it a high-flow engineering plastic suitable for complex, thin-walled products.
Balanced mechanical properties. As a commonly used PC/ABS material, Lotte INFINO WP-1069 has a flexural modulus of 2,300 MPa and a Charpy impact strength (V-notched) of 48 kJ/m², offering excellent rigidity and strength. It is suitable for applications requiring high impact resistance.

Why choose Baiyou as Lotte INFINO WP-1069 PC/ABS supplier?

Leading polycarbonate alloy resin supplier (PC/ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Lotte INFINO WP-1069 PC/ABS
Product information
Manufacturer		Lotte Chemical company
Other Certificates		MSDS
Part Marking Code		>PC/ABS material<
Color		Natural color
Material Shape		PC/ABS Pellets
Process		Injection molding
Features		·High liquidity
Physical properties	Standard	Value	Unit
Specific gravity	ASTM D792	1.13
Melt flow index at 250℃/10kg	ASTM D1238	47	g/10min
Mold shrinkage (MD), flow at 3.2 mm	ASTM D955	0.4-0.7	%
Mold shrinkage (TD), X-flow at 3.2 mm	ASTM D955	0.4-0.7	%
Mechanical behavior	Standard	Value	Unit
Tensile strength, yield, 50 mm/min	ASTM D638	580	kgf/c㎡
Tensile strain, break, 50 mm/min	ASTM D638	80	%
Tensile modulus	ASTM D638	20500	kgf/c㎡
Tensile strength, break, 50 mm/min	ASTM D638	800	kgf/c㎡
Flexural strength	ASTM D790	560	kgf/c㎡
Flexural modulus	ASTM D790	20500	kgf/c㎡
Impact	Standard	Value	Unit
Izod impact strength, notched 1/4 inch at 23℃	ASTM D256	43	kgf·cm/cm
Izod impact strength, notched 1/8 inch at 23℃	ASTM D256	58	kgf·cm/cm
Izod impact strength, notched 1/4 inch at -30℃	ASTM D256	20	kgf·cm/cm
Izod impact strength, notched 1/8 inch at -30℃	ASTM D256	40	kgf·cm/cm
Rockwell hardness, R-Scale	ASTM D785	113
Thermal	Standard	Value	Unit
Heat deflection temperature, 178.56 kgf/c㎡, 6.4 mm	ASTM D638	108	℃
Vicat softening temperature, B/50	ISO 306	123	°C