Asahi Kasei Leona FR370 PA66 | UL 94 V-0

 Asahi Kasei Leona FR370 PA66 Description 

Asahi Kasei Leona FR370 PA66 Advantage

• Flame retardant nylon, Asahi Kasei offers high-performance flame retardancy, achieving UL 94 V-0 flame retardancy at a test thickness of 0.75 mm, the Glow wire flammability index (GWFI) under 3 mm is 960°C, making it suitable for the production of thin-walled flame-retardant products; In addition, this material uses MCA halogen-free flame retardants, which do not release toxic chemicals during the flame-retardant process. It offers exceptional safety performance and is suitable for use in regions with stringent environmental regulations, such as Europe and the United States.
• Excellent electrical performance. Asahi Kasei FR370 PA66-FR has a comparative tracking index (CTI) of 600 V at 3 mm, a surface resistivity of 1.0 × 10¹³ Ω·cm, and a volume resistivity of 1.0 × 10¹⁴ Ω·cm, delivering high-level insulation performance that makes it ideal for use in electronic components and electrical equipment applications.

Why choose Baiyou as Asahi Kasei Leona FR370 PA66 pellets supplier?

• Leading flame retardant nylon supplier (FR PA 66 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Asahi Kasei Leona FR370 PA66
Product information
Manufacturer		Asahi Kasei engineering plastics
Other Certificates		MSDS
Part Marking Code		>PA66-FR material<
Color		Natural color
Material Shape		Nylon 66 Pellets
Process		Injection molding
Features		·No halogen ·Flame retardant ·UL 94 V-0
Application		·Connector ·Electrical / Electronic applications ·Electrical parts ·Switches
Physical properties	Standard	Value		Unit
Melt Density / Specific gravity	ASTM D792	1.16		g/cm³
Molding shrinkag, flow	Internal method	0.90-1.6		%
Water absorption equilibrium, 23% 50% RH	ISO 62	2.3		%
Hardness	Standard	Dry	Conditioned	Unit
Rockwell hardness, M-Scale	ASTM D785	85	55
Rockwell hardness, R-Scale	ASTM D785	120	110
Mechanical behavior	Standard	Dry	Conditioned	Unit
Tensile Modulus 23℃	ISO 527-1	3600	1600	MPa
Tensile stress yield, 23℃	ISO 527-2	83	55	MPa
Tensile stress	ASTM D638	80	-	MPa
Tensile strain yield, 23℃	ISO 527-2	4.5	22	%
Tensile strain break, 23℃	ISO 527-2	415	>50	%
Tensile strain break	ASTM D638	7.0	70	%
Flexural modulus	ASTM D790	3300	1300	MPa
Flexural modulus, 23℃	ISO 178	3600	1500	MPa
Flexural strength	ASTM D790	128	56	MPa
Flexural strength, 23℃	ISO 178	124	54.1	MPa
Taber abrassion resistance, 1000 cycles	ASTM D1044	-	7	mg
Impact	Standard	Dry	Conditioned	Unit
Charpy notched impact strength	ISO 179	4.0	6.0	MPa
Charpy unnotched impact strength	ISO 179	58	No break	kJ/㎡
Notched Izod impact	ISO 179	29	58	J/m
Thermal	Standard	Value		Unit
Deflection temperature, under 0.45 MPa, unannealed	ASTM D648	240		°C
Deflection temperature, under 0.45 MPa, unannealed	ISO 75-2/B	239		°C
Deflection temperature, under 1.8 MPa, unannealed	ASTM D648	80		°C
Deflection temperature, under 1.8 MPa, unannealed	ISO 75-2/B	78		°C
Electrical	Standard	Value		Unit
Surface resistivity	ASTM D257	1.0E+13		ohms
Volume resistivity	ASTM D257	1.0E+14		ohms·cm
Dielectric strength	ASTM D149	31		kV/mm
Comparative tracking index	IEC 60112	600		V
Flammability	Standard	Value		Unit
Flame rating, 0.75mm	UL94	V-0
Glow wire flammability index, 3.0mm	IEC 60695-2-12	960		°C
Oxygen index	ASTM D2863	36		%
Flammability	Standard	Value		Unit
Drying temperature		80-90		°C
Drying time		2-3		hr
Processing temperature		265-275		°C
Mold temperature		75-85		°C

⚠️The technical data sheet (TDS) of Asahi Kasei Leona FR370 flame retardant nylon material from Asahi Kasei engineering plastics, if there are differences, please refer to the official website of Asahi Kasei.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated