LG LUMID GP2301BF PA66

 LG LUMID GP2301BF PA66 pellet Description 

LG LUMID GP2301BF PA66 Advantage

• GF30 PA66, The LG GP2301BF contains 30% glass fiber reinforcement, giving it greater strength, good dimensional stability, higher heat resistance compared to conventional polyamide materials.
• Flame retardant. LG LUMID GP2301BF GF30 PA66 achieves UL94 V-0 flame retardancy at a thickness of 0.75 mm, making it suitable for the production of mechanical components that require high-temperature resistance and flame retardancy, such as automotive engines and home appliance motors.
• High temperature resistance PA66. Compared to unfilled nylon, LG LUMID GP2301BF PA66 material, reinforced with 30% glass fiber, offers superior heat resistance, with a heat deflection temperature of 255°C under a 0.45 MPa test standard, making it ideal for mechanical components used in high-temperature applications.

Why choose Baiyou as LG LUMID GP2301BF PA66 pellets supplier?

• Leading flame retardant nylon 66 polymer supplier (FR PA66 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

LG LUMID GP2301BF PA66
Product information
Manufacturer		LG chemical
Other Certificates		MSDS
Part Marking Code		>GF30 PA66 material<
Color		Natural color
Material Shape		Nylon 66 Pellets
Process		Injection molding
Features		·GF30 reinforced ·UL94 V-0 flame retardant
Application		·Auto ·Chassis & Engine ·HVAC
Physical properties	Standard	Value	Unit
Density 23℃	ASTM D792	1.63	g/cm³
Shrinkage flow at 2.0mm	ASTM D955	0.3~0.5	%
Shrinkage xflow at 2.0mm	ASTM D955	0.3~0.5	%
Melt Index 190°C 21.6kg	ASTM D1238	28	g/10min
Water absorption, 23℃ 50RH	ASTM D570	1.2	%
Hardness	Standard	Value	Unit
Rockwell hardness R-Scale	ISO 2039	120
Mechanical behavior	Standard	Value	Unit
Tensile strength 4.0mm, 5mm/min beak	ISO 527	180	MPa
Tensile elongation 4.0mm, 1mm/min beak	ISO 527	2.8	%
Tensile modulus 4.0mm, 1mm/min	ISO 527	11,000	MPa
Flexural strength 4.0mm, 2.0mm/min	ISO 178	270	MPa
Flexural modulus 4.0mm, 2.0mm/min	ISO 178	11,000	MPa
Izod impact strength, 4.0mm, notched 23℃	ISO 179	11	kJ/㎡
Izod impact strength, 4.0mm, notched -30℃	ISO 179	10	kJ/㎡
Charpy impact strength, 4.0mm, notched 23℃	ISO 179	11	kJ/㎡
Charpy impact strength, 4.0mm, notched -30℃	ISO 179	10	kJ/㎡
Thermal	Standard	Value	Unit
Melt temperature, Peak	ASTM D3418	260	°C
Heat deflection temperature, 0.45MPa, 6.4mm unannealed	ASTM D648	255	°C
Heat deflection temperature, 1.8MPa, 6.4mm unannealed	ASTM D648	249	°C
Vicat sofening temperature 5kg.50 ℃/hr	ASTM D1525	234	°C
Coefficient of linear thermal expansion. -30~80℃ flow	ASTM D696	28	10⁻⁶m/m℃
Coefficient of linear thermal expansion. -30~80℃ xflow	ASTM D696	69	10⁻⁶m/m℃
Electrical properties	Standard	Value	Unit
Comparative tracking index	IEC 60112	250	V
Dielectric constant,10⁶Hz, 23℃	ASTM D150	3
Dielectric strength,1mm, 23℃	ASTM D149	22	kV/mm
Volume resistivity, 23℃	ASTM D257	1.0E+14	ohm-cm
Flammability	Standard	Value	Unit
Flame rating, 3.0mm	UL 94	V-0
Flame rating, 1.5mm	UL 94	V-0
Flame rating, 0.75mm	UL 94	V-0
Injection molding process guidance	Standard	Value	Unit
Back pressure electric type		100-300	kg/cm³
Back pressure hydraulic type		10-30	kg/cm³
Drying temperature		80-100	℃
Drying time		4-5	h
Front cylinder temperature		270-285	℃
Melt temperature		270-290	℃
Middle cylindertemperature		270-280	℃
Moisture content (Max)		0.12	%
Mold temperature		80-110	℃
Nozzle temperature		270-290	℃
Rear cylinder temperature		265-275	℃
Screw speed		60-150	rpm

⚠️The technical data sheet (TDS) of LG LUMID GP2301BF UL94 V-0 flame retardant nylon 66 polymer (PA66 material) from LG chemical , if there are differences, please refer to the official website of LG chemical.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated