Badamid A70 MoS₂ PA66

 Badamid A70 MoS₂ PA66 Description 

Badamid A70 MoS₂ PA66 Advantage

• Good wear resistance, Badamid A70 MoS₂ PA 66, due to its molybdenum disulfide (MoS₂) lubricant content, offers superior wear resistance and lubricity compared to conventional polyamides, reducing the coefficient of friction to 0.03–0.08. It is particularly suitable for components in equipment requiring high-speed motion.
• High load capacity, Unlike wear-resistant PA 66, which uses graphite as a lubricant, Badamid A70 MoS₂ employs molybdenum disulfide as a lubricant, giving it superior load-bearing capacity and making it suitable for use in equipment subjected to high-load dry friction, such as heavy-duty gears and bushings.

Why choose Baiyou as Badamid A70 MoS₂ PA66 pellets supplier?

• Leadingwear resistance nylon pellets supplier (MoS₂ PA 66 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Badamid A70 MoS₂ PA66
Product information
Manufacturer		Bada AG
Other Certificates		MSDS
Part Marking Code		>PA 66+MoS₂ material<
Color		Black
Material Shape		PA 66 Pellets
Process		Injection molding
Features		·High wear resistance ·Lubricated ·MoS₂ reinforced ·Good thermal stability ·High rigidity
Physical properties	Standard	Value		Unit
Density 23℃	ISO 1183	1140		kg/m³
Water absorption	ISO 62	8.5		%
Humidity absorption	ISO 62	2.8		%
Hardness	Standard	Value		Unit
Shore Hardness D	ASTM D2240	68
Mechanical behavior	Standard	Dry	Wet	Unit
Tensile Modulus	ISO 527	3150	1600	MPa
Yield stress	ISO 527	80	60	MPa
Yield strain	ISO 527	4.5	2.1	%
Charpy impact strength, -30℃	ISO 179/1eU	N	N	kJ/㎡
Charpy impact strength, 23℃	ISO 179/1eU	N	N	kJ/㎡
Charpy notched impact strength, -30℃	ISO 179/1eA	4.0	6.0	kJ/㎡
Charpy notched impact strength, 23℃	ISO 179/1eA	6.0	14.0	kJ/㎡
Nominal strain at break, conditioned 23℃ 50% R.F.	ISO 527	min.50		%
Izod notched impact strength, 23℃	ISO 180/1eA	5.0	11.0	%
Izod notched impact strength, 23℃	ISO 180/1eA	3.0	3.0	%
Nominal strain at break, dry as molded	ISO 527	25		%
Thermal	Standard	Value		Unit
Coefficient of linear thermal expansion, parallel	ISO 11359-1/-2	85		E-6/K
Temperature of deflection under load (1.8MPa)	ISO 75-1/-2	75		℃
Temperature of deflection under load (0.45MPa)	ISO 75-1/-2	210		℃
Melting temperature, 10℃/min 0.8mm	ISO 11357-1/-3	262		℃
Burning behavior at thickness	IEC 60695-11-10	V-2
Burning behavior at 1.5mm nominal thickness	IEC 60695-11-10	V-2
Electrical properties	Standard	Dry	Wet	Unit
Surface resistivity	IEC 60093	1.00E+10		ohm
Volume resistivity	IEC 60093	1E13	1E10	ohm

⚠️The technical data sheet (TDS) of Badamid A70 MoS₂ PA66 material from Bada AG, if there are differences, please refer to the official website of Bada.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated