Torayca 3101T-30V PA 6,6 | CF30 reinforced

Material attribute: 30% carbon fiber reinforced; Abrasion resistant; Fatigue resistant

Package: 25 KG/Bag

Process: Injection molding

Get Quotation

Torayca 3101T-30V PA66 Description

Torayca 3101T-30V is a polyamide (CF30 PA66) produced by Toray Industries, Inc. that contains 30% short carbon fiber reinforcement. The material offers excellent wear resistance, fatigue resistance, dimensional stability, and electrical conductivity, and is commonly used in automotive applications, bearings, gears, computer components, and 3D printing applications.

Torayca 3101T-30V PA66 Advantage

CF30 PA66, Torayca 3101T-30V PA 6,6 material contains 30% short carbon fibers, giving it superior mechanical properties and dimensional stability compared to conventional nylon.
High wear resistance. Toray 3101T-30V exhibits a wear rate of only 0.6 mg/hr compared to S45C and a coefficient of friction of just 0.23 compared to S45C—significantly lower than that of conventional nylon materials—making it ideal for small bearings and gear applications that require wear resistance and lubricity.
Conductive.Torayca 3101T 30V PA 6,6 contains carbon fiber, which gives it excellent electrical conductivity, making it suitable for applications requiring low-resistance materials, such as radar electronics housings, EMI shielding components for battery packs, and high-voltage connectors.

Why choose Baiyou as Torayca 3101T-30V PA66 supplier?

Leading carbon fiber reinforced nylon 6,6 supplier (CF30 PA6,6 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Torayca 3101T-30V PA66
Product information
Manufacturer		Toray industries, Inc
Other Certificates		MSDS
Part Marking Code		>CF30-PA66 material<
Color		Gray
Material Shape		CF30 PA 6,6 Pellets
Process		Injection molding
Features		·Abrasion resistant ·Fatigue resistant ·High rigidity ·Low shrinkage
Application		·Automotive applications ·Gears ·Computer components ·Printer
Physical properties	Standard	Value	Unit
Density	ASTM D972	1270	kg/m³
Mold shrinkage across flow, 3.0mm	Internal method	0.7	%
Mold shrinkage flow, 3.0mm	Internal method	0.2	%
Water absorption, 23℃ saturation	ISO 62	1.8	%
Impact	Standard	Value	Unit
Charpy notched impact strength, 23℃	ISO 179	10	kJ/㎡
Mechanical behavior	Standard	Value	Unit
Flexural Modulus 23 ℃	ISO 178	20000	MPa
Tensile Strength 23 ℃	ISO 527-2	255	MPa
Flexural stress 23 ℃	ISO 178	350	MPa
Tensile strain 23℃, break	ISO 527-2	1.6	%
Amount of wear - vs. S45C	Suzuki method	0.6	mg/hr
Coefficient of friction - vs. S45C	Suzuki method	0.23
Limiting pressure velocity - vs. S45C	Suzuki method	2.6	MPa·m/s
Electrical	Standard	Value	Unit
Volume resistive	JIS K7194	0.010	ohms·m
Surface resistive	JIS K7194	10	ohms/c㎡
Thermal	Standard	Value	Unit
Deflection temperature under 1.8 MPa, unannealed	ISO 75-2/A	255	℃
Melting temperature	DSC	265	℃
CLTE flow	ISO 11359-2	1.6	cm/cm℃
CLTE transverse	ISO 11359-2	1.9	cm⁻⁵/cm/℃
Flame rating , 0.79mm	UL 94	HB

⚠️The technical data sheet (TDS) of Torayca 3101T-30V carbon fiber reinforced nylon (CF30 PA66) material from Toray industries,Inc , if there are differences, please refer to the official website of Toray.