Formosa Tairilac AG15A1-H ABS

Application: Universal materials

Melt flow rate: 23g/10min (220℃ 10kg)

Packing:25KG/Bags

Process:Injection molding

Get Quotation

Formosa Tairilac AG15A1-H ABS Description

Tairilac AG15A1-H is a general purpose grade acrylonitrile-butadiene-styrene resin (ABS material) produced by Formosa Chemical & Fiber Corporation. It features a melt index of 23 (at 220°C, 10kg) and offers balanced mechanical properties and high gloos, suitable for manufacturing ABS products with high aesthetic requirements and a high-gloss finish.

Tairilac AG15A1-H ABS is manufactured at two locations: Taiwan and Ningbo, China. Generally, we give priority to supplying ABS material produced in Ningbo, China.

As shown in the image on the left, Tairilac AG15A1-H natural ABS consists of milky white, roughly cylindrical pellets. High-gloss black is also available. . Please let us know if you require a custom color or a specific region of origin.

Formosa Tairilac AG15A1-H ABS Advantage

Good visual properties, Products manufactured using Tairilac AG15A1 ABS material feature a high gloss finish, also has good compatibility with color masterbatches, making it suitable for toys, audio enclosures, suitcases, and other applications demanding superior aesthetic properties.
⚠️The image on the left shows a sample sheet made from Tairilac AG15A1 ABS. It is clear that the material has a high gloss and high reflectivity.
Good mechanical properties. Tairilac AG15A1-H ABS offers performance comparable to that of LG HI-121H, CHIMEI 757, and INEOS Terluran GP-22, while offering a significant price advantage, making it a suitable substitute for these materials.

Why choose Baiyou as Formosa Tairilac AG15A1-H ABS supplier?

Leading high gloss Acrylonitrile-Butadiene-Styrene resin pellets supplier (ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Formosa Tairilac ABS AG15A1-H
Product information
Manufacturer		FORMOSA CHEMICALS & FIBRE CORPORATIO
Other Certificates		REACH
Part Marking Code		>High gloss ABS material<
Color		Natural color
Material Shape		ABS Pellets
Process		Injection molding ABS pellets
Flame Retardant		HB
specification		UL
Features		·High gloss ·High stiffness ·Medium Impact ·General purpose grade
Application		·General purpose ·Toys
UL File NO.		E162823
Physical properties	Standard	Value	Unit
Density 23°C	ASTM D792	1.05	g/cm³
Density 23°C	ISO 1183	1.05	g/cm³
Melt Index 220°C 10kg	ASTM D1238	23	g/10min
Melt Index 220°C 10kg	ISO 1133	23	g/10min
Melt Index 200°C 5kg	ASTM D1238	2.3	g/10min
Melt Index 200°C 5kg	ISO 1133	2.3	g/10min
Hardness	Standard	Value	Unit
Rockwell Hardness R(Scale) 23°C	ASTM D785	110
Rockwell Hardness R(Scale) 23°C	ISO 2039	110
Mechanical behavior	Standard	Value	Unit
Tensile Strength 23°C	ASTM D638	445	kg/cm²
Tensile Strength 23°C	ISO 527	45	Mpa
Flexural Strength 23°C	ASTM D790	750	kg/cm²
Flexural Strength 23°C	ISO 178	66	Mpa
Flexural Strength 23°C	ASTM D790	25000	kg/cm²
Flexural Strength 23°C	ISO 178	2350	Mpa
Izod Notch Impact 23°C 6.4mm	ASTM D256	25	kg-cm/cm
Izod Notch Impact 23°C 6.4mm	ISO 180	220	J/m
Thermal	Standard	Value	Unit
HDT Unannealed 1.8MPa 120°C/hr 6.4mm	ASTM D648	87	°C
HDT Unannealed 1.8MPa 120°C/hr 6.4mm	ISO 75	87	°C
HDT Annealed 1.8MPa 120°C/hr 6.4mm	ASTM D648	95	°C
HDT Annealed 1.8MPa 120°C/hr 6.4mm	ISO 75	95	°C
Vicat Softening Temperature 50N	ASTM D1525	91	°C
Vicat Softening Temperature 50N	ISO 306	91	°C
Flammability	Standard	Value	Unit
Flame Rating All Color 1.0mm	UL94	HB
Flame Rating All Color 1.6mm	UL94	HB
Flame Rating All Color 3.0mm	UL94	HB