tairilac ag15a0 abs granules

Tairilac AG15A0 ABS

Application: Universal

Melt flow rate: 22g/10min

Packing:25KG/Bags

Process:Injection molding
Get Quotation

Tairilac AG15A0 ABS Description

Application

Tairilac AG15A0 is a kind of ABS resin pellets specially designed for injection molding. The final product has characteristics such as high gloss and smooth surface, and is suitable for products with high requirements on product appearance.

Tairilac AG15A0 ABS Advantage

  • High impact, AG150A ABS products have higher load capacity while minimizing damage when receiving higher impacts.
  • High gloss, the final product has high gloss and smooth surface, suitable for products with high requirements on appearance
  • With high fluidity, AG15A0 is an ABS resin granules with a high melt index, which is suitable for the manufacturing of complex products and can also ensure high production efficiency.

Company Profile 

Baiyou is affiliated to Luoyang Dahao Industry & Trade Company Limited which is a large joint-stock company specializing in chemical raw materials, was established in2003, has 500+employees,20+years of plastic product manufacturing, chemical raw material import and export, and a registered capital of 15 million dollars.

Why choose Baiyou as Tairilac AG15A0 ABS supplier?

  • LeadingABS (Acrylonitrile Butadiene Styrene) resin supplier, 20+ years of experience in plastic product manufacturing and chemical raw material import and export
  • Fastest Arrival, with warehouses in multiple ports
  • 1,000+ types of resin products are available, and we have cooperated with large petrochemical groups for 30+years
  • Free Samples for production testing
  • Wholesale price, even a piece of goods is based on the wholesale price
 Key Attributes 
Tairilac  AG15A0  ABS
Product information
ManufacturerFORMOSA CHEMICALS & FIBRE CORPORATIO
Other CertificatesREACH
Part Marking Code>ABS<
ColorNC
Material ShapeABS Pellets
ProcessInjection molding grade ABS
FRHB
specificationUL
FeaturesGeneral purpose grade;High gloss;  Impact modified
ApplicationGeneral purpose
UL File NO. E162823
Physical propertyStandardValueUnit
Density   23°CASTM D792 1.05 g/cm³
Density   23°CISO 1183 1.05 g/cm³
Melt Index   220°C 10kgASTM D123822g/10min
Melt Index   220°C 10kgISO 113322g/10min
Melt Index   200°C 5kgASTM D12382.2g/10min
Melt Index   200°C 5kgISO 11332.2g/10min
HardnessStandardValueUnit
Rockwell Hardness   R(Scale) 23°CASTM D785110
Rockwell Hardness   R(Scale) 23°CISO 2039110
Mechanical behaviorStandardValueUnit
Tensile Strength   23°CASTM D638445 kg/cm²
Tensile Strength   23°C ISO 52747 Mpa
Flexural Strength   23°C ASTM D790800 kg/cm²
Flexural Strength   23°CISO 17878 Mpa
Flexural Strength   23°CASTM D79027000 kg/cm²
Flexural Strength   23°CISO 178  2650 Mpa
Izod Notch Impact    23°C 6.4mmASTM D25622 kg-cm/cm
Izod Notch Impact    23°C 6.4mmISO 180216 J/m
ThermalStandardValueUnit
HDT   Unannealed 1.8MPa 120°C/hr 6.4mm ASTM D64885°C
HDT   Unannealed 1.8MPa 120°C/hr 6.4mm        ISO 7585°C
HDT   Annealed Annealed at 80°C for 8 hoursASTM D64895°C
HDT   Annealed Annealed at 80°C for 8 hours ISO 7595°C
Vicat Softening Temperature   10NASTM D1525100°C
Vicat Softening Temperature   10N ISO 306100°C
FlammabilityStandardValueUnit
Flame Rating   All Color 1.5mmUL94HB
Flame Rating   All Color 3.0mmUL94HB 
 
 Partners  
We have established long-term relationships with 80+ well-known  companies around the world
Warehouse And Shipping  
26 years' experience Professional purchasing consultant with a supply chain of 1000+ plastic raw materials in China.
Quantity (tonnes)1-100100-300>300
Lead time (days)7-10
10-15
To be negotiated