Taitalac 5000W ABS

Application: Office application, Home appliance application

Melt flow rate: 19 cm³/10min

Packing: 25KG/Bags

Process: Injection molding

Get Quotation

Taitalac 5000W ABS Description

Taitalac 5000W is injection molding Acrylonitrile Butadiene Styrene (ABS) resin raw material, with high fluidity and high gloss characteristics. Taita 5000W is the first choice for producing high precision, complex products with high requirements on appearance quality.

Taitalac 5000W ABS Advantage

Good processing conditions, Taitalac 5000W ABS material has a melt index of 19cm³/10min at 220℃ 10kg test environment, suitable for injection molding processing, and is very suitable for the production of complex and precise parts.
Good appearance properties. Compared with conventional ABS materials, products made of Taitalac 5000W ABS materials have smooth surfaces and fewer defects, which has great advantages in application scenarios with more stringent requirements on appearance.
Excellent high temperature resistance. Compared with conventional ABS materials, Taitalac 5000W ABS has a softening concentration of 102°C under a 50°C/hr 10N test environment. It can be used in office equipment, electronic and electrical equipment, and home appliance housings that require heat dissipation.

Why choose Baiyou as Taitalac 5000W ABS pellets supplier?

Leading ABS (Acrylonitrile Butadiene Styrene) resin supplier, 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

TAITALAC® ABS 5000W
Product information
Manufacturer		Taita Chemical Company, Ltd.
Other Certificates		MSDS
Part Marking Code		>ABS material<
Color		WT Colors available
Material Shape		Pellets
Process		Injection molding ABS
FR		HB
Material Attribute		Injection grade ABS pellets
Specification		UL
Features		·High gloss ·High flow
Application		·Office Applications ·E & E applications ·Appliances ·Home appliances applications ·Housewares application
UL File NO		E50263
Physcial properties	Standard	Value	Unit
Density 23°C	ISO 1183	1.03	g/cm³
Shrinkage Flow 60x60x2mm	ISO 294	0.4	%
Humidity Absorption 23°C 50RH Equilibrium	ISO 62	0.3	%
Melt Index 220°C 10kg	ISO 1133	19	cm³/10min
Hardness	Standard	Value	Unit
Rockwell Hardness R(Scale) 23°C	ISO 2039	110
Mechanical behavior	Standard	Value	Unit
Tensile Strength Yield 23°C 50mm/min	ISO 527	48	Mpa
Tensile Strength Break 23°C 50mm/min	ISO 527	37	Mpa
Elongation Break 23°C 50mm/min	ISO 527	30	%
Flexural Strength Yield 23°C 2.0mm/min	ISO 178	76	Mpa
Flexural Modulus 23°C 2.0mm/min	ISO 178	2.2	Gpa
Izod Notch Impact 23°C	ISO 180	19	kJ/m²
Charpy Notch Impact 23°C	ISO 179	20	kJ/m²
Thermal	Standard	Value	Unit
Heat deflection temperature (HDT) Unannealed 1.8MPa	ISO 75	85	°C
Vicat Softening Temperature 50°C/hr 10N	ISO 306	102	°C
Flammability	Standard	Value	Unit
Flame Rating All Color 1.5mm	UL94	HB
Flame Rating All Color 3.0mm	UL94	HB
Injection molding		Value	Unit
Dry Temperature		80~85	°C
Dry Time		2~4	hr
Zone1 Temperature		170~180	°C
Zone2 Temperature		185~215	°C
Zone3 Temperature		195~225	°C
Zone4 Temperature		185~215	°C
Nozzle Temperature		205~235	°C
Mould Temperature		40~70	°C
Injection Pressure		Moderate
Injection Speed		Moderate-Fast
Screw Speed		30~100	rpm
Back Pressure		50~70	psi