Chimei Polylac PA-777E ABS | Ultra heat resistant
Material attribute: Ultra heat resistant; High strength
Package: 25KG/Bag
Melt flow index (MFI): 4.0g/10min (at 200℃ 10kg)
Package: 25KG/Bag
Melt flow index (MFI): 4.0g/10min (at 200℃ 10kg)
Chimei Polylac PA-777E ABS pellet Description
Polylac PA-777E is an acrylonitrile-butadiene-styrene resin (ABS material) produced by Chimei corporation with superb high-temperature resistance properties, and is commonly used in the production of automotive parts, office equipment, appliance housings, and hair dryer housings, etc., because of its high high temperature resistance properties and strength.
Chimei Polylac PA-777E ABS Advantage
- High temperature resistant ABS material，Compared with conventional ABS materials, Chimei PA-777E ABS material has more excellent high temperature resistance properties, the heat distortion temperature under 1.8MPa annealed condition reaches 120℃, even if the heat distortion temperature without annealing treatment can reach 109℃, and the vicat softening temperature under the 50℃/hr 10N test standard can reach 29℃, which is much higher than conventional ABS materials. Can reach 29 ℃, much higher than the conventional ABS materials, suitable for the need to dissipate the heat of home appliances shell, office equipment shell, hair dryer shell use.
- Balanced mechanical properties. Chimei polylac high temperature resistant ABS material 777E has a rockwell hardness of 115, a flexural strength of 700kg/c㎡ and a flexural modulus of 2.3GPa under a 2.8mm/min test environment, which is a very strong hardness and rigidity suitable for use in It has strong hardness and rigidity and is suitable for the use of equipment shells that are impact resistant, dimensionally stable, not easily deformed, and resistant to high temperature.
Why choose Baiyou as Chimei Polylac PA-777E ABS pellets supplier?
- Leading heat resitant Acrylonitrile-butadiene-styrene pellets supplier (ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
- Fastest Arrival, with warehouses in multiple ports
- 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
- Free Samples for production testing
- Wholesale price, even a piece of goods is based on the wholesale price
Key Attributes
| Chimei Polylac PA-777E ABS | |||
| Product information | |||
| Manufacturer | Chimei Corporation | ||
| Other Certificates | MSDS RoHS REACH | ||
| Part Marking Code | >Heat resistant ABS material< | ||
| Material Shape | ABS Pellets | ||
| Flame retardant | HB | ||
| Process | Injection molding grade | ||
| Material attribute | ·High heat resistant grade ·Injection molding grade | ||
| specification | RoHS UL | ||
| Features | ·High strength ·Ultra high heat resistant | ||
| Application | ·Automotive parts ·Office applications ·E&E housing ·Home appliance housing ·Compacting equipment ·Hairdryer housing ·Motorcycle parts | ||
| Additives | ·Heat stabilizer ·Lubricant ·Mold release | ||
| Physical properties | Standard | Value | Unit |
| Density 23℃ | ASTM D792 | 1.07 | g/cm³ |
| Shrinkage | ISO 294 | 0.3~0.6 | % |
| Melt Index 220℃ 10kg | ASTM D1238 | 4 | g/10min |
| Hardness | Standard | Value | Unit |
| Shore Hardness R(Scale) | ASTM D785 | 115 | |
| Mechanical behavior | Standard | Value | Unit |
| Tensile strength yield 6mm/min | ASTM D638 | 450 | kg/c㎡ |
| Tensile Strength Yield 50mm/min | ISO 527 | 45 | Mpa |
| Tensile Strength break 50mm/min | ISO 527 | 32 | Mpa |
| Elongation 6mm/min | ASTM D638 | 10 | % |
| Elongation 50mm/min | ISO 527 | 29 | % |
| Flexural strength 2.8mm/min | ASTM D790 | 700 | kg/c² |
| Flexural strength 2.0mm/min | ISO 178 | 74 | MPa |
| Flexural modulus 2.8mm/min | ASTM D790 | 23000 | kg/c㎡ |
| Flexural modulus 2.0mm/min | ISO 178 | 2.3 | GPa |
| Izod Notch Impact 23℃ 6.4mm | ASTM D256 | 11 | kg-cm/cm |
| Izod Notch Impact 23℃ 3.2mm | ASTM D256 | 12 | kg-cm/cm |
| Izod Notch Impact 23℃ | ISO 180 | 12 | kJ/㎡ |
| Izod Notch Impact -30℃ | ISO 180 | 6 | kJ/㎡ |
| Charpy notch impact 23℃ | ISO 179 | 13 | kJ/㎡ |
| Charpy notch impact -30℃ | ISO 179 | 6 | kJ/㎡ |
| Thermal | Standard | Value | Unit |
| HDT annealed 1.8MPa | ASTM D648 | 120 | ℃ |
| HDT unannealed 1.8MPa | ASTM D648 | 109 | ℃ |
| Vicat Softening Temperature 50℃/hr 10N | ASTM D1525 | 129 | ℃ |
| Vicat Softening Temperature 50℃/hr 50N | ISO 306 | 121 | ℃ |
| CLE | ISO 11359 | 8.2E-5 | cm/cm/℃ |
| Flammability | Standard | Value | Unit |
| Flame retardant all color 1.5mm | UL94 | HB | |
| Flame retardant all color 3.0mm | UL94 | HB | |
⚠️The technical data sheet (TDS) of Sabic B5428 high density polyethylene material from Saudi basic industry, if there are differences, please refer to the official website of Sabic.
Partners
We have established long-term relationships with 80+ well-known companies around the world |
Warehouse And Shipping
20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China. |
Quantity (tonnes) | 1-100 | 100-300 | >300 |
Lead time (days) | 7-10 | 10-15 | To be negotiated |
Best Selling Product