LG GN1001BF PA66

 LG GN1001BF PA66 pellet Description 

LG GN1001BF PA66 Advantage

• UL94 V0 flame retardant PA66. LG GN1001BF PA66 material has been tested to achieve UL94 V-0 flame retardancy, making it suitable for applications with stringent flame retardancy requirements such as electronic components, electrical appliances, and automotive parts. Additionally, this material is free of halogens and brominated flame retardants, meeting high-performance environmental standards and qualifying for use in regions with stringent environmental regulations like Europe and the United States.

Why choose Baiyou as LG GN1001BF PA66 pellets supplier?

• Leading flame retardant nylon 66 resin pellets supplier (FR PA66 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

LG GN1001BF PA66
Product information
Manufacturer		LG chemical
Part Marking Code		>PA66 material<
Color		Natural color
Material Shape		PA66 Pellets
Process		Injection molding nylon 66
Features		·Cl, Br free flame retardant agents
Application		·Auto ·Electronics ·Home appliances ·Industrial goods
Physical properties	Standard	Value	Unit
Specific gravity 23℃	ISO 1183	1.15
Shrinkage flow 2.0mm		0.8-1.1	%
Shrinkage cross flow 2.0mm		0.7-1.1	%
Water absorption 23℃ 50% RH	ISO 62	2.50	%
Hardness	Standard	Value	Unit
Rockwell hardness R-scale	ISO 2039	112
Mechanical behavior	Standard	Value	Unit
Tensile strength at Yield, 4.0mm, 50mm/min	ISO 527	15	MPa
Tensile elongation at Break, 4.0mm, 50mm/min	ISO 527	108	MPa
Tensile modulus, 4.0mm 1mm/min	ISO527	108	MPa
Flexural strength, 4.0mm 2.0mm/min	ISO 178	2800	MPa
Izod impact strength, 4.0mm notched 23℃	ISO 180	5.5	kJ/㎡
Izod impact strength, 4.0mm notched -30℃	ISO 180	4.5	kJ/㎡
Charpy impact strength, 4.0mm notched 23℃	ISO 179	4.9	kJ/㎡
Charpy impact strength, 4.0mm notched -30℃	ISO 179	3.4	kJ/㎡
Thermal	Standard	Value	Unit
Vicat Softening Temperature 50N 50℃/hr	ISO 306	219	°C
Heat deflection temperature (HDT) 0.45 MPa 4mm,flatwise unannealed	ISO 75	209	°C
Heat deflection temperature (HDT) 1.8 MPa 4mm,flatwise unannealed	ISO 75	61	°C
Coefficient of linear thermal expansion flow -30℃-80℃	ISO 11359	61	10⁻⁶m/m·℃
Coefficient of linear thermal expansion cross flow -30℃-80℃	ISO 11359	89	10⁻⁶m/m·℃
Flammability	Standard	Value	Unit
Flame rating at 0.75-0.82mm	UL94	V-0
Electrical	Standard	Value	Unit
Comparative tracking index (CTI), solution A	UL746A	0	PLC
Dielectric constant 23℃	ASTM D150	3.0
Dielectric constant 23℃ 2.0mm	ASTM D149	22	KV/mm
Injection molding guidance	Standard	Value	Unit
Drying temperature		80-100	℃
Drying time		4-5	hrs
Maximum moisture content		0.12	%
Melt temperature		260-280	℃
Cylinder temperature rear		255-270	℃
Cylinder temperature middle		260-275	℃
Cylinder temperature front		260-275	℃
Nozzle temperature		270-280	℃
Mold temperature		60-90	℃

⚠️The technical data sheet (TDS) of LG GN1001BF flame retardant nylon 66 (PA66 material) from LG chemical, if there are differences, please refer to the official website of LG Chem.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated