Lotte Starex TX-0520IM MABS | Transparent

 Lotte Starex TX-0520IM MABS pellet Description 

Lotte Starex TX-0520IM MABS Advantage

• Excellent transparency, Compared to conventional ABS materials, the greatest advantage of MABS lies in its transparency.Lotte TX-0520IM MABS material achieves 90% light transmittance with a haze level of only 2.0% at a 3200μm test thickness. It offers excellent transparency and visual properties, making it suitable for applications demanding high aesthetic standards such as transparent toys and transparent casings with printed graphics.
• Excellent machinability，Lotte Starex TX-0520 MABS material exhibits a melt flow index of 18g/10min (MFI 18) under a 220°C, 10kg test environment, indicating moderate flow rate. It is suitable for injection molding processes and compatible with most injection molding equipment, offering broad applicability.

Why choose Baiyou as Lotte Starex TX-0520IM MABS pellets supplier?

• Leading Methyl methacrylate-acrylonitrile-butadiene-styrene resin pellets supplier (transparency  ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Lotte Starex TX-0520IM MABS
Product information
Manufacturer		Lotte chemical corporation
Other Certificates		MSDS
Part Marking Code		>Transparent ABS material<
Color		Transparency with blue tint
Material Shape		MABS Pellets
Process		Injection molding
Material attribute		·Injection molding ·Transparent ABS
specification		UL
Physical properties	Standard	Value	Unit
Density 23℃	ASTM D792	1.09	g/cm³
Linear mold shrinkage, transverse 2mm	ASTM D294	0.6	%
Linear mold shrinkage, flow 2mm	ASTM D294	0.4	%
Melt Index 220°C 10kg	ASTM D1238	18	g/10min
Hardness	Standard	Value	Unit
Rockwell hardness	ASTM D785	108
Mechanical behavior	Standard	Value	Unit
Flexural modulus at 2mm/min	ISO 178	2200	Mpa
Flexural strength at 2mm/min	ISO 178	70	Mpa
Tensile Strength at Yield	ISO 527	47	Mpa
Impact strength notched Charpy at 23℃ 4.0mm	ISO 179	12	kJ/㎡
Impact strength notched Izod at 23℃ 4.0mm	ISO 179	12	kJ/㎡
Modulus of elasticity at 5mm/min	ISO 527	1900	Mpa
Tensile strain at break at 5mm/min	ISO 527	20	%
Tensile strength at break at 5mm/min	ISO 527	40	Mpa
Optical performance	Standard	Value	Unit
Transmittance	ASTM D1003	90	%
Haze 3200μm	ASTM D1003	2.00	%
Thermal	Standard	Value	Unit
Vicat Softening Temperature 50℃/hr 50N	ISO 306	91	°C
HDT unannealed 0.45MPa 6.4mm	ISO 75	82	°C
HDT unannealed 1.8MPa 6.4mm	ISO 75	71	°C
Flammability	Standard	Value	Unit
Flame rating all color 1.5mm	UL94	HB
Flame rating all color 3.0mm	UL94	HB
Injection molding	Standard	Value	Unit
Back pressure		5-20kgf/c㎡
Cylinder zone 1 temperature		230℃
Cylinder zone 2 temperature		210-220℃
Cylinder zone3 temperature		200-210℃
Drying temperature		85℃
Dry time, dehumidifying dryer		4h
Dry time, normal hopper dryer		4h
Hot runner temperature, valve nozzle		240℃
Hot runner temperature, manifolder		240℃
Injection pressure		750-2400kgf/c㎡
Moisture content		0.05%
Mold temperature		90%
Nozzle temperature		240℃
Screw ratation speed		30-70rpm

⚠️The technical data sheet (TDS) of Lotte Starex TX-0520IM transparency MABS material from Lotte chemical, if there are differences, please refer to the official website of Lotte chemical.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated