Qatar Lotrène FD0274 LDPE

 Qatar Lotrène FD0274 LDPE pellet Description 

Lotrène FD0274 film grade LDPE material (low density polyethylene resin pellet) is produced by QAPCO Qatar petrochemical company, containing lubricant and anti-blocking agent ingredients, has excellent gloss and transparency and is often used to produce very thin, high-transparency films.

Qatar Lotrène FD0274 LDPE pellet Advantage

• Film grade LDPE materia, As an LDPE material specifically designed for film and packaging bags, FD0274 LDPE has excellent mechanical propertiesandgood tensile properties and puncture resistance at 40μm. In blown film testing, the tensile strength at break in the flow direction is 24MPa and in the perpendicular direction is 22MPa. The elongation at break in the flow direction is 300% and in the perpendicular direction is 600%, which provides good processing conditions for stretch film manufacturing.

• Good processing performance. Lotrene FD0274 LDPE material, melt index 2.4g/10min, is suitable for blow molding and compression molding processing. It also contains lubricant and anti-blocking agent ingredients, which facilitates film production and storage while also improving customer experience.

Why choose Baiyou as Qatar Lotrène FD0274 LDPE pellets supplier?

• Leading film grade low density polyethylene resin pellet supplier (LDPE resin) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Qatar Lotrène LDPE  FD0274
Product information
Manufacturer		Qatar Petrochemical Company (QAPCO) QsC
Other Certificates		MSDS
Part Marking Code		>LDPE material<
Process		·Extrusion molding ·Compression Molding ·Foam Molding
Material Attribute		·Film grade ·Antiblock ·Food Contact grade
Application		Film ·Foam products ·Food packaging ·Deep freeze
Physical propertis	Standard	Value	Unit
Density  23°C	ASTM D1505	0.923	g/cm³
Melt Index	ASTM D1238	2.4	g/10min
Mechanical behavior	Standard	Value	Unit
Tensile Strength Flow Yield 40um Blown Film	ASTM D882	11	Mpa
Tensile Strength xFlow Yield 40um Blown  Film	ASTM D882	11	Mpa
Tensile Strength Flow Break 40um Blown Film	ASTM D882	24	Mpa
Tensile Strength xFlow Break 40um Blown Film	ASTM D882	22	Mpa
Elongation Flow Break 40μm Blown Film	ASTM D882	300	%
Elongation xFlow Break 40μm Blown FiIm	ASTM D882	600	%
Tearing Strength Flow 40μm Blown Film	ASTM D1922	65	N/mm
Tearing Strength xFlow 40μm Blown Film	ASTM D1922	35	N/mm
Falling Weight Impact strength 40μm Blown Fim	ASTM D1709	110	g
Friction Coefficient 40um Blown Film	ASTM D1894	0.12
Puncture Resistance Force 40um Blown Film	INTERNAL METHOD	30	N
Optical performance	Standard	Value	Unit
Gloss 45°40um Blown Film	ASTM D2457	5.9
Haze 40um Blown Film	ASTM D1003	8	%
Thermal	Standard	Value	Unit
Vicat Softening Temperature	ASTM D1525	89	°C
Melting Temperature	ASTM E794	108	°C

⚠️The technical data sheet (TDS) of Qatar Lotrène FD0274 film grade low density polyethylene material, from Qatar petrochemical company, if there are difference, please refer to the official website of Qatar petrochemical.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated