Asahikasei Leona 1300S PA66

Density: 1.14 g/cm³

Water Absorption: 2.5 %

Packing: 25KG / Bag

Process: Injection molding

Get Quotation

AsahiKasei Leona 1300S PA66 pellet Description

Leona 1300S is injection molding polyamide 6,6 (PA66) produced by Japan Asahi Kasei. It contains mold release and lubricant ingredients, has excellent toughness, electrical properties, and good heat and oil resistance. Leona 1300S PA6,6 material is commonly used in the production of automotive parts, automotive interior and exterior trim, rolled strip, and office equipment parts.

AsahiKasei Leona 1300S PA66 pellet Advantage

High-temperature resistant PA66 material. Compared with other plastic materials, Leona 1300S PA6/6 has better heat resistance. The heat deformation temperature under 0.45MPa test environment reaches 190℃, and the heat deformation temperature under 1.8MPa test environment reaches 70℃.
Good flexibility. The tensile modulus of Asahi Kase 1300S PA6/6 material in the dry state under the test environment of 23℃ reaches 3000MPa, and the flexural modulus reaches 2700MPa. It is convenient for product bending and stretching processing while having good impact absorption capacity.
PA6,6 material with excellent lubrication performance and wear resistance. Leona 1300S has a Taber wear of only 7.00 mg after 1000 cycles. At the same time, this material also contains lubricant components, making it very suitable for gears and connector accessories with high lubrication requirements.

Why choose Baiyou as AsahiKasei Leona PA66 pellet supplier?

Leading polyamide 6.6 resin pellets supplier (PA66 / nylon 66 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

AsahiKasei Leona™ PA66 1300S
Product information
Manufacturer		Asahi Kasei Corporation
Part Marking Code		>PA66 material<
Color		Natural Color
Material Shape		PA66 Pellets
Process		Injection molding nylon
Flame retardant		V-2
specification		UL
Features		·Good appearance ·High flow High stiffness· High strength ·High toughness ·Rapid moldability ·External lubrication ·Good processability
Application		·Automotive Interior ·Trim ·Automotive applications ·Automotive parts ·Office Applications ·Fasteners ·Outdoor Cactivities ·Applications ·Coil skeleton ·Connector ·E & E Applications ·Terminal block ·Toys applications ·Home Appliances Applications ·Fittings ·Gears ·Housing Industrial Applications ·Machinery parts ·Luggage ·Baby carriage ·Kitchen Appliances Applications ·Spatula ·Sports goods Applications ·Sports equipment Applications ·Bathroom Applications ·Consumer applications ·Structural Parts Cable ties ·Costumes application
Additives		·Lubricant ·Mold Releases
UL File NO.		E48285
Physical properties	Standard	Value		Unit
Density	ASTM D792	1.14		g/cm³
Density	ISO 1183	1.14		g/cm³
Shrinkage Flow	INTERNAL METHOD	1.3-2.0		%
Water Absorption 23°C Saturation	ISO 62	2.5		%
WaterAbsorption 23°C 50RH Equilibrium	ISO 62	2.5		%
Hardness	Standard	Dry	Wet	Unit
Rockwell Hardness M(Scale)	ISO 2039	80	55
Rockwell Hardness R(Scale)	ASTM D785	120	108
Mechanical behavior	Standard	Dry	Wet	Unit
Tensile Modulus 23°C	ISO 527	3000	1200	MPa
Tensile Strength Yield 23°C	ISO 527	82	52	MPa
Tensile Strength	ASTM D638	79	57	MPa
Elongation Yield 23°C	ISO 527	4	24	%
Elongation Break	ASTM D638	50	250	%
Elongation Break 23°C	ISO 527		100	%
Flexural Strength	ASTM D790	118	54	MPa
Flexural Strength 23°C	ISO 178	113	42	MPa
Flexural Modulus	ASTM D790	2800	1200	MPa
Flexural Modulus 23°C	ISO 178	2700	1100	MPa
Izod Notch Impact	ASTM D256	3.9	150	J/m
Charpy Notch Impact	ISO 179	6	15	kJ/m²
Charpy Un-notch Impact	ISO 179	NB	NB	kJ/m²
Tabor Wear 1000 Cycles	ASTM D1044		7	mg
Thermal	Standard	Value		Unit
HDT Unannealed 0.45MPa	ASTM D648	230		°C
HDT Unannealed 0.45MPa	ISO 75	190		°C
HDT Unannealed 1.8MPa	ASTM D648	70		°C
HDT Unannealed 1.8MPa	ISO 75	70		°C
CLE Flow	ASTM D696	8E-5		cm/cm/°C
Heat Conductivity Coefficient		0.2		W/(m·K)
Specific Heat		1670		J/(kg·°C)
Electrical properties	Standard	Value		Unit
Volume Resistivity	ASTM D257	1E14		Ω.cm
Volume Resistivity 23°C	IEC 60093	1E14		Ω.cm
Surface Resistivity	ASTM D257	1E13		Ω
Surface Resistivity	IEC 60093	1E13		Ω
Dielectric Strength	ASTM D149	20		KV/mm
Dielectric Strength	IEC 60243	20		KV/mm
CTI 3.0mm	IEC 60112	600		V
Flammability	Standard	Value		Unit
GWFI 3.0mm	1EC60695	960		°C
Flame Rating NC 0.40mm	UL94	V-2
Flame Rating All Color 0.71mm	UL94	V-2
Flame Rating All Color 1.5mm	UL94	V-2
Flame Rating All Color3.0mm	UL94	V-2
Limiting Oxygen Index	ASTM D2863	26		%