TAIRILAC AE8000 ABS
Application: Safety helmet,pipe
Melt index: 4.9 g/10min ( 220°C 10kg)
Process: Extrusion molding
Melt index: 4.9 g/10min ( 220°C 10kg)
Process: Extrusion molding
Tairilac AE8000 ABS pellet Description
Tairilac AE8000 is a high-rigidity, impact-resistant acrylic-butadiene-styrene resin pellet (ABS material) manufactured by Formosa Chemical & Fibers Corporation. It features a melt index of 4.9 g/10 min (at 220°C, 10 kg) and is suitable for producing safety helmets, pipes, luggage, and similar applications.
Tairilac AE8000 ABS Advantage
- Highly impact-resistant ABS material，Tairilac AE8000 ABS exhibits exceptional impact resistance, with a flexural modulus of 2156 MPa at 23°C and an Izod notch impact strength of 440 J/m at a test thickness of 6.4 mm. Its impact resistance significantly surpasses conventional ABS materials, making it ideal for manufacturing safety helmets, luggage, and other products with high impact resistance requirements.
Why choose Baiyou as Tairilac AE8000 ABS pellets supplier?
- Leading high impact resistant Acrylonitrile-Butadiene-Styrene pellets supplier (ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
- Fastest Arrival, with warehouses in multiple ports
- 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
- Free Samples for production testing
- Wholesale price, even a piece of goods is based on the wholesale price
Key Attributes
| Tairilac AE8000 ABS | |||
| Product information | |||
| Manufacturer | Formosa chemical & fibre corporation | ||
| Other Certificates | ·MSDS ·REACH | ||
| Part Marking Code | >ABS material< | ||
| Material Shape | ABS Pellets | ||
| Process | Extrusion molding | ||
| Flame retardant | HB | ||
| Specification | UL | ||
| Features | ·High stiffness ·High impact | ||
| Application | ·Safety helmet ·Pipe ·Heels ·Extrusion applications | ||
| Physical properties | Standard | Value | Unit |
| Density 23℃ | ASTM D792 | 1.04 | g/cm³ |
| Shrinkage 3.2mm | ASTM D955 | 0.4~0.7 | % |
| Melt Index 220°C 10kg | ASTM D1238 | 4.9 | g/10min |
| Hardness | Standard | Value | Unit |
| Shore Hardness R(Scale) 23℃ | ASTM D785 | 103 | |
| Mechanical behavior | Standard | Value | Unit |
| Tensile strength 23℃ | ASTM D638 | 43 | Mpa |
| Flexural strength 23℃ | ASTM D790 | 73 | Mpa |
| Flexural Modulus 23℃ | ASTM D790 | 2156 | Mpa |
| Izod Notch Impact 23℃ 6.4mm | ASTM D256 | 440 | J/m |
| Thermal | Standard | Value | Unit |
| HDT unannealed 1.8MPa 6.4mm | ASTM D648 | 87 | ℃ |
| HDT annealed at 80℃ for9 hours | ASTM D648 | 96 | ℃ |
| Vicat Softening Temperature 10N | ASTM D1525 | 102 | °C |
| Flammability | Standard | Value | Unit |
| Flame rating all color 1.6mm | UL94 | HB | |
⚠️The technical data sheet (TDS) of FCFC Tairilac AE8000 high impact resistant ABS material from Formosa chemical & fiber, if there are differences, please refer to the official website of FCFC.
Partners
We have established long-term relationships with 80+ well-known companies around the world |
Warehouse And Shipping
20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China. |
Quantity (tonnes) | 1-100 | 100-300 | >300 |
Lead time (days) | 7-10 | 10-15 | To be negotiated |
Best Selling Product