TAIRILAC AG15E1 ABS

Application: Toys, cell phones, calculators, audio shell

Density: 1.05 g / cm³

Melt index: 25 g/10min ( 220°C 10kg)

Get Quotation

Tairilac AG15E1 ABS pellet pellet Description

Tairilac ABS AG15E1 is an injection molding Acrylonitrile-Butadiene-Styrene resin pellet (ABS material) produced by Formosa Chemical & Fiber. It has good strength and gloss and can be used to produce toys, mobile phones, clocks, calculator casings, etc.

Tairilac AG15E1 ABS pellet Advantage

Good appearance characteristics. Products made of Tairilac AG15E1 ABS material have good gloss and smoothness. They have great advantages in products with high requirements for appearance and are often used in the production of home appliance shells.
Tairilac AG15E1 ABS material has good mechanical strength. The Izod notched impact performance measured by ASTM D256 under a 23°C 6.4mm test environment reaches 137J/m. It is suitable for small device housings with strict requirements on impact resistance and drop resistance.

Why choose Baiyou as Tairilac AG15E1 ABS pellets supplier?

LeadingAcrylonitrile-Butadiene-Styrene resin pellet supplier (ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

TAIRILAC AG15E1 ABS pellets
Product information
Manufacturer		Formosa Chemicals & Fibre Corporation
Part Marking Code		>ABS material<
Material Shape		ABS Pellets
FR		HB
Specification		UL
Features		·High gloss ·High stiffness
Application		·Toys ·Totel bins ·Cell phone ·Calculators ·Audio shell ·Clock housing
Physical properties	Standard	Value	Unit
Density 23°C	ASTM D792	1.05	g/cm³
Shrinkage 3.2mm	ASTM D955	0.4~0.7	%
Melt index 200℃ 5kg	ASTM D1238	2.0	g/10min
Melt Index 220°C 10kg	ASTM D1238	25	g/10min
Mechanical behavior	Standard	Value	Unit
Tensile Strength 23°C	ASTM D638	480	kg/cm²
Tensile strength 23℃	ASTM D638	48	MPa
Flexural Strength 23°C	ASTM D790	840	kg/cm²
Flexural strength 23℃	ASTM D790	83	MPa
Flexural Modulus 23°C	ASTM D790	28000	kg/cm²
Flexural modulus 23℃	ASTM D790	2750	MPa
Izod notch impact 23℃ 6.4mm	ASTM D256	14	kg-cm/cm
Izod notch impact 23℃ 6.4mm	ASTM D256	137	J/m
Thermal	Standard	Value	Unit
Vicat Softening Temperature 10N	ASTM D1525	103	°C
HDT unannealed 1.8MPa 6.4mm	ASTM D648	85	℃
HDT annealed at 80℃ for 8 hours	ASTM D648	95	℃