Trinseo Magnum 8391 ABS

 Trinseo Magnum 8391 ABS pellet Description 

Trinseo Magnum 8391 ABS Advantage

• Excellent appearance properties, Products made from Trinseo Magnum 8391 ABS exhibit excellent gloss, making them suitable for manufacturing appliance housings and toys with high aesthetic requirements. This ABS material also offers superior colorability, enabling manufacturers to easily adjust material hues.
• Excellent mechanical properties.
  Trinseo Magnum 8391 ABS material offers excellent strength and impact resistance, with a flexural modulus of 2480 MPa in a 3.2 mm test environment. and a Charpy notched impact strength of 19 kJ/m² when injection molded at 23°C. Even at extreme low temperatures of -30°C, it maintains an impact strength of 9 kJ/m². This material is suitable for manufacturing toys and appliance housings requiring high impact resistance.
• High liquidity,Trinseo 8391 ABS material exhibits a melt flow index (MFI or MVR) of 28g/10min under a 220°C, 10kg test environment. This material is suitable for injection molding processes, and its strong flow properties enable the production of thin-walled products.

Why choose Baiyou as Trinseo Magnum 8391 ABS pellets supplier?

• Leading Acrylonitrile-Butadiene-Styrene resIn pellets supplier (ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

Trinseo Magnum 8391 ABS
Product information
Manufacturer		Trinseo PLC
Part Marking Code		>ABS material<
Color		Natural color
Material Shape		ABS Pellets
Process		Injection molding
Features		·High glossy performance ·High flow ·Medium impact resistance
Application		·Hosehold appliances ·Consumer goods ·Toys
Physical properties	Standard	Value	Unit
Density	ASTM D792	1.05	g/cm³
Apparent density	ISO 60	0.65	g/cm³
Melt mass - flow rate (MFR) 220℃/10kg	ASTM D1238	28	g/10min
Melt mass - flow rate (MFR) 230℃/3.8kg	ASTM D1238	8	g/10min
Molding shrinkage - flow	ASTM D955	0.40-0.70	%
Hardness	Standard	Value	Unit
Rockwell hardness (R-Scale)	ASTM D785	108
Mechanical behavior	Standard	Value	Unit
Tensile Modulus 3.2mm, injction molded	ISO 527-2	2340	MPa
Tensile Strength Yield	ASTM D638	48.0	MPa
Tensile Strength Yield, 3.2mm, injection molded	ISO 527-2/50	45.0	MPa
Tensile Strength Yield, 3.2mm, injection molded	ISO 527-2/100	47.0	MPa
Tensile Strength Break	ASTM D638	35.0	MPa
Tensile Elongation Yield	ASTM D638	2.7	%
Tensile Elongation Yield, 3,2mm, injection molded	ISO 527-2/50	2.5	%
Tensile Elongation Yield, 3.2mm, injection molded	ISO 527-2/100	2.6	%
Flexural Modulus	ASTM D790	2480	MPa
Flexural Modulus, 3,2mm, injection molded	ISO 178	2400	MPa
Flexural Strength	ASTM D790	75.0	MPa
Flexural Strength, 3,2mm, injection molded	ISO 178	70.0	MPa
Charpy notched impact strength, -30℃, injection molded	ISO 179/1eA	9.0	kJ/㎡
Charpy notched impact strength, 23℃, injection molded	ISO 179/1eA	19	kJ/㎡
Notched izod impact, 23℃, injection molded	ASTM D256	230	kJ/㎡
Notched izod impact, -30℃, injection molded	ISO 180/A	9.0	kJ/㎡
Notched izod impact, 23℃, injection molded	ISO 180/A	19	kJ/㎡
Izod Notch Impact	ASTM D256	130	J/m
Thermal	Standard	Value	Unit
Deflection temperature Under load, 0.45MPa, unannealed	ASTM D648	87.0	°C
Deflection temperature Under load, 1.8MPa, unannealed	ASTM D648	87.0	°C
Deflection temperature Under load, 1.8MPa, annealed	ISO 75-2/A	87.0	°C
Vicat softening temperature	ASTM D1525	99	°C
Vicat softening temperature	ISO 306/B50	95	°C
Flammability	Standard	Value	Unit
Burning rate 2.0mm	ISO 3795	60	mm/min
Flame rating 1.5mm	UL94	HB
Flame rating 3.0mm	UL94	HB

⚠️The technical data sheet (TDS) of Trinseo Magnum 8391 ABS material from Trinseo PLC, if there are differences, please refer to the official website of  Trinseo.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated