BASF Ultramid A3EG6 PA66 | GF30 reinforced

Application: Mechanical parts, cooling system parts

Density: 1.36 g/cm³

Water Absorption: 5.2~5.8 %

Packing: 25KG / Bag

Process: Injection molding

Get Quotation

BASF Ultramid A3EG6 PA66 pellet Description

Application

BASF Ultramid A3EG6 Injection molding nylon 66 material, adding 30% glass fiber to enhance rigidity and high temperature resistance, contains release agent and lubricant ingredients, easy to process plastic products, used to manufacture heat dissipation components and insulation components

BASF Ultramid A3EG6 PA66 pellet Advantage

High temperature resistance: Ultramiad A3EG6 polyamid material is reinforced with 33% glass fiber, which is more resistant to high temperatures than the same nylon material without glass fiber. It is suitable for manufacturing wear-resistant mechanical parts and cooling system parts.
Easy to process. The melt index of the BASF A3EG6 material reaches 30g/10min, and the fluidity is relatively high during processing. At the same time, the nylon material contains a release agent, which is suitable for the manufacture of precision and complex products.
Nylon material with enhanced mechanical properties. After being reinforced with glass fiber, the rigidity and strength of A3EG6 PA66 are significantly improved. The finished products hardly deforms under high temperature and long-term stress. The material has excellent stability and is suitable for various engineering applications.

Why choose Baiyou as BASF Ultramid PA66 pellets supplier?

Leading polyamide 6/6 supplier (PA6/6 resin) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

BASF Ultramid PA66 A3EG6
Product information
Manufacturer		BASF Corp.
Part Marking Code		>PA66 material<
Color		natural color
Material Shape		PA66 Pellets
Process		Injection molding nylon 66
FR		HB
specification		UL UL-746C F1
Features		·Dimensional stability ·High flow ·High stiffness ·Heat aging resistant ·Hot water resistance ·Good weather resistance
Application		·Automotive cooling units ·Radiator tank ·Electrically insulating parts ·Insulation ·Housing ·Machine mechanical parts ·Aluminum window frames ·Lamp socket housings ·Cooling fan
Additives		·Heat stabilizer ·Lubricant ·Mold Releases
UL File NO.		E41871
Physical properties	Standard	Value		Unit
Density	ISO 1183	1.36		g/cm³
Shrinkage	INTERNAL ETHOD	0.55		%
Shrinkage flow	ISO 294	0.53		%
Shrinkage xflow	ISO 294	1.02		%
Water Absorption 23°C Saturation in water	ISO 62	5.2~5.8		%
Melt index 275℃ 5kg	ISO 1133	30		cm³/10min
Viscosity number 0.5% in 96 H₂SO₄	ISO 307	145		cm³/g
Halogen content Cl Br I	Internal method	100		ppm
Mechanical behavior	Standard	Value	Wet	Unit
Tensile Modulus 23°C	ISO 527	10000	7200	MPa
Tensile Strength break	ISO 527	190	130	MPa
Elongation Break	ISO 527	3	5	%
Tensile creep modulus 1000hr 23℃ 0.5% strain	ISO 899		5300	MPa
Flexural Strength	ISO 178	280	210	MPa
Flexural Modulus	ISO 178	8600	6500	MPa
Izod Notch Impact 23℃	ISO 180	12	15	kJ/㎡
Izod Notch Impact -30℃	ISO 180	10.4	10	kJ/㎡
Charpy Notch Impact 23℃ 1eA	ISO 179	13	12	kJ/m²
Charpy Notch Impact -30℃ 1eA	ISO 179	11	9.5	kJ/m²
Charpy Un-notch Impact 23 ℃	ISO 179	85	100	kJ/m²
Charpy Un-notch Impact 23 ℃	ISO 179	70	70	kJ/m²
Thermal	Standard	Value		Unit
HDT 1.8MPa	ISO 75	250		°C
HDT 0.45MPa	ISO 75	260		°C
Melt temperature DSC	ISO 11357	260		°C
Melt temperature		290		°C
CLE Flow 23~80℃	ISO 11359	2.8E-5		m/m/K
CLE xFlow 23~80℃	ISO 11359	8.8E-5		m/m/K
Heat Conductivity Coefficient	DIN 52612	0.35		W/(m·K)
Specific Heat	INTERNAL METHOD	1260		J/(kg·°C)
Service temperature short time	INTERNAL METHOD	240		℃
Service temperature 5000hr	IEC 60216	165		℃
Service temperature 20000hr	IEC 60216	135		℃
Electrical properties	Standard	Wet		Unit
Volume Resistivity	IEC 62631	1E10		Ω.cm
Surface Resistivity	IEC 62631-3-2	1E10		Ω
Dielectric Strength 0.6-0.8mm K20/P50	IEC 60243	80		KV/mm
Dielectric Strength 60601mm K20/P50	IEC 60243	37		KV/mm
Dielectric constant 1MHz	IEC 62631-2-1	4.3
Dissipation factor 1MHz	IEC 62631-2-1	0.081
CTI solution A	IEC 60112	550		V
Flammability	Standard	Value		Unit
Flame Rating All Color 0.75mm	UL94	HB
Flame Rating All Color 1.5mm	UL94	HB
Flame Rating All Color 3.0mm	UL94	HB
Flame Rating All Color 6.0mm	UL94	HB