Celanese Fortron 1140L4 PPS | GF40 reinforced

Application: Automotive applications; Autotive heaters; Bobbins; E&E applications; Lampshade; Valves; Water pump parts; Microware oven rings; Fuel rails

Packing: 25KG/Bag

Process: injection Molding

Get Quotation

Polyplastics Durafide 1140A6 HD9100 PPS pellet Description

Application

Fortron 1140L4 is a PPS material produced by Celanese Company that focuses on injection molding. 1140L4 PPS has the characteristics of high strength, high hardness, high toughness, wear resistance, and chemical resistance. Due to its good performance, it is widely used in many fields such as automotive parts, home appliance parts, valves, and water pump parts.

Celanese Fortron 1140L4 PPS pellet Advantage

With super high temperature resistance, Fortron 1140L4 PPS products can still maintain good mechanical properties in high continuous use temperature (160℃ to 240℃) working environment, and play an excellent heat resistance. It has full application in high temperature use environment such as automobile parts manufacturing and industrial equipment parts.
Ultra-high strength plastic material. Fortron 1140L4 is reinforced with 40% glass fiber to effectively enhance the strength of the material. It has the highest strength among similar products and is a project material in automotive parts, electrical parts and industrial equipment applications.
High-performance flame-retardant material. Celanese 1140L4 has a UL94 flame-retardant rating of V-0,5VA, which is a high flame-retardant material among polyphenylene sulfide materials of the same grade. It is widely used in home appliances and automobiles.
Good processing performance. To improve the processing of PPS materials, 1140L4 PPS is added with a release agent, which plays an advantage in large-scale production, precision and small parts manufacturing.
Excellent dimensional stability. 1140L4 PPS has a small thermal expansion coefficient and low water absorption. It is almost non-deformed after manufacturing and is suitable for applications with strict dimensional requirements.

Company Profile

Baiyou is affiliated to Luoyang Dahao Industry & Trade Company Limited which is a large joint-stock company specializing in chemical raw materials, was established in2003, has 500+employees,20+years of plastic product manufacturing, chemical raw material import and export, and a registered capital of 15 million dollars.

Why choose Baiyou as Celanese Fortron 1140L4 PPS pellets supplier?

Leading PPS pellets supplier (Polyphenylene Sulfide) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Product information
Celanese Fortron 1140L4 PPS
Manufacturer		Celanese corporation
Part Marking Code		>polyphenylene material<
Material Shape		PPS pellets
Process		Injection molding PPS pellets
Material Attribute		40%glass fiber reinforced; flame retardant; Heat resistant;Drinking water contact
Features		Weldable; Chemical resistant; Good electrical properties； High strength; High hardness; High stiffnesss; Hightoughness
Application		Automotive applications; Autotive heaters; Bobbins; E&E applications; Lampshade; Valves; Water pump parts; Microware oven rings; Fuel rails
Additives		Mold releases
Physical property	Standard	Value	Unit
Density	ISO 1183	1.65	g/cm³
Shrinkage flow	ISO 294	0.3	%
Shrinkage xflow	ISO 294	0.6	%
Water absorption 23℃ saturation	ISO 62	0.02	%
Bulk density	ISO 60	0.721	g/cm³
Hardness	Standard	Value	Unit
Rockwell Hardness M（scale）	ISO 2039	100
Mechanical behavior	Standard	Value	Unit
Tensile strength	ISO 527	14700	MPa
Tensile strength break 5mm/min	ISO 527	195	MPa
Elongation break 5mm/min	ISO 527	1.9	%
Flexural strength break	ISO 178	285	MPa
Flexural modulus 23℃	ISO 178	14000	MPa
Izod notch impact 23℃ Type A	ISO 180	10	kJ/㎡
IZod notch impact -30℃ Type A	ISO 180	10	kJ/㎡
Izod un-notch impact 23℃	ISO 180	34	kJ/㎡
Izod un-notch impact -30℃	ISO 180	34	kJ/㎡
Charpy Notch impact 23℃ 1eA	ISO 179	10	kJ/㎡
Charpy Notch impact -30℃ 1eA	ISO 179	10	kJ/㎡
Charpy un-notch impact 23℃	ISO 179	53	kJ/㎡
Charpy un-notch impact -30℃	ISO 179	53	kJ/㎡
Compressive modulus	ISO 604	15000	MPa
Thermal	Standard	Value	Unit
HDT 1.8 MPa	ISO 75	270	℃
HDT 8.0MPa	ISO 75	215	℃
Melt temperature 10℃/min	ISO 11357	280	℃
Glass transition temperature 10℃/min	ISO 11357	90	℃
CLE Flow	ISO 11359	2.6E-5	cm/cm*/℃
CLE xFlow	ISO 11359	4.2E-5	cm/cm*/℃
Specific heat melt	internal method	1500	J(kg·K)
Electrical properties	Standard	Value	Unit
Volume resistivity	IEC 60093	1E+13	Ω·cm
Surface resistivity	IEC 60093	6.6E+11	Ω·cm
Dielectric strength	IEC 60243	28	KV/mm
Dielectric constant 1MHz	IEC 60250	4.1
Dissipation Factor 1MHz	IEC 60250	0.002
CTI rating	UL 746A	4	PLC
Flammability	Standard	Value	Unit
Flame rating all color 0.38mm	UL94	V-0
Flame rating all color 0.81mm	UL94	V-0
Flame rating all color 1.5mm	UL94	V-0
Flame rating all color 3.0mm	UL94	V-0 5VA