RADILON S RV300 333 NER PA6 | GF30

 RADILON S RV300 333 NER PA6 pellet Description 

RADILON S RV300 333 NER PA6 Advantage

• GF30 PA6, RADILON S R300 333 NER contains 30% glass fiber reinforcement, providing superior rigidity and enhanced heat resistance compared to conventional nylon 6 materials.
  At 2 mm/min, its flexural modulus reaches 8550 MPa, and at 1 mm/min, its modulus of elasticity reaches 9600 MPa, providing excellent rigidity and structural stability. This makes it ideal for producing load-bearing structural components, positioning it as an outstanding engineering plastic.
  In an unannealed state, the heat deflection temperature reaches 200°C at 1.8 MPa, with a Vicat softening temperature of 210°Cat 50°C/h. This makes it suitable for automotive components and mechanical parts with demanding temperature requirements.

Why choose Baiyou as RADILON S RV300 333 NER PA6 pellets supplier?

• Leading 30% glass fiber reinforced nylon 6 resin pellets supplier (GF30 PA6 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
• Fastest Arrival, with warehouses in multiple ports
• 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
• Free Samples for production testing
• Wholesale price, even a piece of goods is based on the wholesale price

---

 Key Attributes 

RADILON S RV300 333 NER PA6
Product information
Manufacturer		Radici Group
Other Certificates		RoHS
Part Marking Code		>Nylon 6 material<
Color		Natural color
Material Shape		GF30 PA6 Pellets
Process		Injection molding
Features		·30% glass fiber reinforced ·High stiffness
Application		·Automotive ·Technical ·Ondustrial ·Building ·Sports ·Furnishing applications
Physical properties	Standard	Value	Unit
Density	ISO 1183	1.35	g/cm³
Moisture absorption, at 23℃ 50%RH, 2mm	ISO 62	2	%
Water absorption, at 23℃ 24hr, 2mm	ISO 62	7.5	%
Hardness	Standard	Value	Unit
Shore Hardness D	ASTM D2240	68
Mechanical behavior	Standard	Value	Unit
Flexural modulus at 2mm/min	ISO 178	8500	MPa
Flexural strength at 2mm/min	ISO 178	245	MPa
Impact strength, notched charpy at 23℃	ISO 179	11	kJ/㎡
Impact strength, notched charpy at -30℃	ISO 179	9	kJ/㎡
Impact strength, unnotched charpy at 23℃	ISO 179	68	kJ/㎡
Impact strength, unnotched charpy at -30℃	ISO 179	60	kJ/㎡
Modulus of elasticity at 1mm/min	ISO 527-2	9600	MPa
Tensile strain at break, 23℃	ISO 527-2	3.1	%
Tensile strength at break, at 5mm/min	ISO 527-2	175	MPa
Thermal	Standard	Value	Unit
Vicat Softening Temperature at 50℃/h, B(50N)	ISO 306-2	210	°C
Heat deflection temperature (HDT), unannealed at 1.8MPa	ISO 75-2A	200	°C
Heat deflection temperature (HDT), unannealed at 0.45MPa	ISO 75-2-B	215	°C
Melting point 10℃/min	ISO 11357-3	220	°C
Flammability	Standard	Value	Unit
Automotive interior flammability	FMVSS302	0	mm/min
Flame rating at 0.8mm	UL94	HB
Glow wire flammability index (GWFI) at 2mm	IEC 60695-2-1/2	700	℃
Electrical properties	Standard	Value	Unit
Comparative tracking index (CTI) Solution A	IEC 60112	500
Surface resistance at 23℃ 500V	IEC 60093	1E+12	ohm
Volume resistance at 23℃ 500V	IEC 60093	1E+13	ohm-m
Injection molding process guidelines	Standard	Value	Unit
Dew point of the dryer		0-20	°C
Drying temperature		80	°C
Drying time		2-4	h
Melt temperature		240-280	°C
Moisture content (Max)		0.15	%
Mold temperature		80-90	°C

⚠️The technical data sheet (TDS) of RADILON S RV300 333 NER 30% glass fiber reinforced nylon 6 resin (GF30 PA6 material) RadiciGroup, if there are differences, please refer to the official website of Radici.

 Partners 

We have established long-term relationships with 80+ well-known  companies around the world

 Warehouse And Shipping 

20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.

Quantity (tonnes)	1-100	100-300	>300
Lead time (days)	7-10	10-15	To be negotiated