Toray Amilan CM1017 PA6

Material attribute: ·Flame retardant ·UL 94 V-2

Package: 25 KG/Bag

Process: Injection

Get Quotation

Toray Amilan CM1017 PA6 Description

Amilan CM1017 is unfilled nylon 6 material manufactured by Toray Industries, Inc. It features high flowability, high strength, high flexibility, high-temperature resistance, and wear resistance. It meets the UL 94 V-2 flame-retardant rating and can be used in home appliances, household goods, and automotive applications.

Toray Amilan CM1017 PA6 Advantage

Flame retardant V2 Nylon, Toray CM1017 PA 6 material features high-temperature resistance and flame retardancy, with deflection temperature of 190°C at 0.45 MPa. At thickness of 0.75 mm, it achieves UL 94 V-2 flame retardancy, making it suitable for use in home appliance and automotive components that require heat resistance, heat dissipation, and flame retardancy.
Good mechanical properties. Toray CM1017 nylon 6 resin is used in a wide range of applications due to its outstanding performance. With a tensile strength of 85 MPa and a flexural modulus of 120 MPa, its high mechanical strength makes it suitable for high-load-bearing components in industries such as machinery and automotive.

Why choose Baiyou as Sabic Toray Amilan CM1017 PA6 supplier?

Leading polyamide 6 resin supplier (PA6 material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Toray Amilan CM1017 PA6
Product information
Manufacturer		Toray industries Inc
Other Certificates		MSDS
Part Marking Code		>PA6 material<
Color		·Natural color ·Black
Material Shape		PA6 Pellets
Process		Injection molding
Features		·High liquidity ·Contains mold release
Applications		·Appliance components ·Construstion applications ·Sporting goods ·Autonmotive applications ·Electrical/Electonic applications ·Tanks ·Automotive electronics ·Fuel lines ·White good & small appliances ·Automotive interior parts ·Office automation equipment ·Windows & doors ·Automotive under the hood ·Seats
Physical properties	Standard	Value		Unit
Density	ISO 1183	1130		kg/m³
Melt volume rate, MVR at 300℃/1.2kg	ISO 1133	21		cm³/10min
Mold shrinkage, 1.0 mm	Toray METHOD	0.5-1.0		%
Mold shrinkage, 3.0 mm	Toray METHOD	1.0-1.6		%
Spiral flow	Toray METHOD	670		mm
Water absorption 24 hr, 23℃	ISO 62	1.8		%
Water absorption saturation, 23℃	ISO 62	10.5		%
Mechanical behavior	Standard	Dry	Wet absorption	Unit
Hardness Rockwell 23℃, R-Scale	ISO 2039-2	119	90
Hardness Rockwell 80℃, R-Scale	ISO 2039-2	83	-
Tensile strength, -40℃	ISO 527-2	120	115	MPa
Tensile strength, 23℃	ISO 527-2	85	40	MPa
Tensile strength, 80℃	ISO 527-2	30	20	MPa
Tensile strain, 23℃, yield	ISO 527-2	1.5	-	%
Tensile strain, 23℃, break	ISO 527-2	38	＞50	%
Flexural modulus, -40℃	ISO 178	3900	3600	MPa
Flexural modulus, 23℃	ISO 178	3000	1000	MPa
Flexural modulus, 80℃	ISO 178	800	400	MPa
Flexural stress, -40℃	ISO 178	145	140	MPa
Flexural stress, 23℃	ISO 178	120	45	MPa
Flexural stress, 80℃	ISO 178	50	30	MPa
Compressive stress, 23℃	ISO 604	85	-	MPa
Shear strength, 23℃	ASTM D732	75	70	MPa
Taber abrasion resistance, 1000 cycles	ISO 9352	3 to 4	-	mg
Coefficient of friction vs metal	Suzuki METHOD	0.15 to 0.20	-
Impact	Standard	Dry	Wet absorption	Unit
Charpy notchedd impact strength, -40℃	ISO 179	2.5	11.5	kJ/㎡
Charpy notchedd impact strength, 23℃	ISO 179	4.0	31.0	kJ/㎡
Charpy unnotchedd impact strength, -40℃	ISO 179	No break	-
Charpy unnotchedd impact strength, 23℃	ISO 179	No break	-
Thermal	Standard	Value		Unit
Melting temperature	DSC	225		°C
Specific heat		1900		J/kg/°C
Thermal conductivity		0.25		W/m/K
Coefficient of linear thermal expansion	ISO 11359-2	8		cm/^-5/cm/℃
Electrical	Standard	Dry	Water absorption	Unit
Volume resistivity	IEC 60093	>1.E+12	>1.E+9	ohms·m
Electric strength	IEC 60243	20	-	kV/mm
Dielectrics constant, 23℃ 50 Hz	IEC 60250	4.1	9.0	kV/mm
Dielectrics constant, 23℃ 1 kHz	IEC 60250	3.9	8.0	kV/mm
Dielectrics constant, 23℃ 1 MHz	IEC 60250	3.4	4.5	kV/mm
Dissipation factor, 23℃ 50 Hz	IEC 60250	0.070	0.100
Dissipation factor, 23℃ 1 kHz	IEC 60250	0.060	0.110
Dissipation factor, 23℃ 1 MHz	IEC 60250	0.030	0.130
Arc resistance	UL 746	120	-	sec
Comparative tracking index (CTI)	UL 746A	＞600	-	V
Flame retardant	Standard	Value		Unit
Flame rating, 0.75 mm	UL 94	V-2