KINGFA KF-730 ABS

Application: General purpose grade

Process: Injection molding

Package: 25 KG/Bag

Get Quotation

KINGFA KF-730 ABS Description

KF-730 is a general-purpose injection-molded acrylonitrile-butadiene-styrene (ABS material) resin manufactured by Kingfa Sci.&Tech. Co., Ltd. It has a melt flow index of 2 and is suitable for use in housings for home appliances, office equipment, and electronic devices.

KF 730 ABS is manufactured at KINGFA’s factory in China. As shown in the image on the left, it comes in the form of nearly cylindrical granules and is milky white in color.

👉Please contact us if you require a custom color.

KINGFA KF-730 ABS Advantage

Balanced attributes, Kingfa 730 ABS has an Izod notched impact strength of 20 kJ/m² and a tensile strength of 47 MPa. Based on its mechanical properties, it can be used as a substitute for general-purpose ABS grades such as Terluran GP22, Chimei PA-727, and Tairilac ABSAG15A1.
Good machinability. The melt mass flow rate (MFR) of KF-730 ABS is 2 g/10 min under test conditions of 200°C and 5 kg; it has a moderate flow rate and is suitable for conventional injection molding equipment.

Why choose Baiyou as KINGFA KF-730 ABS supplier?

Leading Acrylonitrile-Butadiene-Styrene resin supplier (ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

KINGFA KF-730 ABS
Product information
Manufacturer		KINGFA science & technology company
Other Certificates		MSDS
Part Marking Code		>ABS material<
Color		·Natural color
Material Shape		ABS Pellets
Process		Injection molding
Physical properties	Standard	Value	Unit
Density, 23 ℃	ISO 1183	1050	kg/m³
Melt mass volume rate, MFR at 200℃/5kg	ISO 1133	2.0	cm³/10min
Melt mass volume rate, MFR at 200℃/10kg	ISO 1133	20	cm³/10min
Mold shrinkage, 23℃	ISO 2577	0.4-0.7	%
Mechanical behavior	Standard	Value	Unit
Tensile strength, 50 mm/min	ISO 527	47	MPa
Tensile strain at break, 50 mm/min	ISO 527	8	MPa
Flexural strength, 2 mm/min	ISO 178	76	MPa
Flexural modulus, 2 mm/min	ISO 178	2500	MPa
Rockwell hardness, R-Scale	ISO 20392	108	MPa
Izod notched impact strength, 23℃	ISO 180	20	kJ/㎡
Thermal	Standard	Value	Unit
Vicat Softening Temperature,1kg 120℃/h	ISO 306	96	°C
Vicat Softening Temperature, 1kg 50℃/h	ISO 306	86	°C
Heat Deflection Temperature, 0.45 MPa	ISO 75-2	85	℃
Heat Deflection Temperature, 1.8 MPa	ISO 75-2	77	℃
Electrical	Standard	Value	Unit
Volume resistivity	IEC 60093	1E14	Ω.cm
Dielectrics strength	IEC 60243-1	22	kV/mm
Flame retardant	Standard	Value	Unit
Flammability, 1.6 mm	UL 94	HB
Injection molding guidance	Standard	Value	Unit
Drying temperature		80--90	℃
Drying time		2-4	hrs
Maximum moisture content		0.02	%
Melt temperature		215	℃
Nozzle temperature		270-290	℃
Front - Zone 3 temperature		180-200	℃
Middle - Zone 2 temperature		190-210	℃
Rear- Zone 1 temperature		195-220	℃
Processing temperature upper limit		250	℃
Mold temperature		30-60	℃
Back pressure		0-1000	KPa