LG LUPOY PC 1302-05 PC

Material attribute: ·High impact resistance ·UV resistance

Melt index: 5 g/10min (300℃ 1.2kg)

Applications: Sheet

Get Quotation

LG LUPOY PC 1302-05 PC Description

LUPOY PC 1302-05 is an extrusion-grade polycarbonate resin manufactured by LG Chem, also known as"PC material."It features UV resistance and can be used to produce PC multilayer sheets and PC solid sheets.

LG LUPOY PC 1302-05 PC Advantage

Good processability, As a polycarbonate material specifically designed for the extrusion molding of sheet stock, LG LUPOY 1302-05 PC has a melt flow rate (MFR) of 5 g/10 min at 300°C with a load of 1.2 kg. It is suitable for conventional sheet extrusion processing equipment and resists warping and deformation during the production of wide-width sheets. Its processing properties are similar to those of the more commonly used Makrolon ET3117 PC, making it a direct substitute.
UV resistance. LG 1302-05 PC resin contains UV stabilizers and is particularly suitable for the production of sun panels and corrugated sheets for outdoor use.

Why choose Baiyou as LG LUPOY PC 1302-05 PC supplier?

Leading polycarbonate resin supplier (PC material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

LG LUPOY PC 1302-05 PC
Product information
Manufacturer		LG Chem
Other Certificates		MSDS
Part Marking Code		>PC material<
Color		Transparent polycarbonate
Material Shape		PC Pellets
Process		Extrusiong molding
Features		·High impact strength ·UV stabilized
Physical properties	Standard	Value	Unit
Density	ASTM D792	1200	kg/m³
Melt flow rate, MVR at 300℃/1.2kg	ASTM D1238	5	g/10min
Mold shrinkage	ASTM D955	0.005-0.007	mm/mm
Water absorption @ 24 hrs, 23℃	ASTM D570	0.15	%
Water absorption @ equilibrium, 50%RH, 23℃	ASTM D570	0.32	%
Mechanical behavior	Standard	Value	Unit
Tensile strength, yield	ASTM D638	60	MPa
Ultimate Tensile strength	ASTM D638	72	MPa
Elongation at yield	ASTM D638	6	%
Elongation at break	ASTM D638	150	%
Tensile modulus	ASTM D638	2410	MPa
Flexural strength	ASTM D790	96	MPa
Flexural modulus	ASTM D790	2410	MPa
Notched Izod impact @ 23℃	ASTM D256	950	J/m
Unnotched Izod impact @ 23℃	ASTM D256	No break	J/m
Instrumented dart impact, total energy @ 23℃	ASTM D3763	94	J
Rockwell hardness @ R Scale	ASTM D785	118
Rockwell hardness @ M Scale	ASTM D785	74
Taber abrasion resistance (D Haze)	ASTM D1044	45	%
Thermal	Standard	Value	Unit
Deflection temperature under load (DTUL) @ 4 mm 66 psi (0.45 MPa), annealed	ASTM D648	146	°C
Deflection temperature under load (DTUL) @ 4 mm 264 psi (1.8 MPa), annealed	ASTM D648	143	°C
Deflection temperature under load (DTUL) @ 4 mm 264 psi (1.8 MPa), UNannealed	ASTM D648	132	°C
Vicat sofening point, 50 ℃/hr， 50N load	ASTM D1525	151	°C
Coefficient of linear thermal expansion, @ -40 to 82 ℃	ASTM D696	68× 10^-6	mm/mm/℃
Electrical	Standard	Value	Unit
Volume resistivity @ 23℃, dry	ASTM D257	2.0×10^17	Ω.cm
GWT 2.0 mm, 5 second	IEC 695-2-1	850	℃
Dielectrics strength	ASTM D149	17	kV/mm
Comparative tracking index @ 2.0 mm	IEC 112	250
Dissipation factor, 60 Hz	ASTM D150	0.001
Dielectrics factor, 60 Hz	ASTM D150	3
Flame retardant	Standard	Value	Unit
UL-94 @ 0.5 mm	ASTM D635	V-2
UL-94 @ 1.6 mm	ASTM D635	V-2
UL-94 @ 2.5 mm	ASTM D635	V-2
UL-94 @ 3.0 mm	ASTM D635	V-2
Limiting oxygen index	ASTM D2863	26	%
Ball indentation temperature	IEC 598-2-1	>125	℃
Average extent of buring	ASTM D635	25	mm
Optical	Standard	Value	Unit
Refractive index, nD	ASTM D542	1.586
Haze	ASTM D1003	0.7-1.5	%
Light transmittance	ASTM D1003	89	%