Sabic Lexan 920A-116 PC

Material attribute: ·UL 94 V-0 flame retardant ·Transparent

Package: 25 KG/Bag

Process: Injection molding

Get Quotation

Sabic Lexan 920A-116 FR PC Description

Lexan 920A-116 medium viscosity polycarbonate (PC) material manufactured by Saudi Basic Industries Corporation. UL 94 V-0 flame retardant rating, transparent color, melt index of 15, suitable for injection molding.

Sabic Lexan 920A-116 FR PC Advantage

UL 94 V-0 flame retardant, Lexan 920A-116 PC contains 0.3 phr of KSS (sulfonate-based flame retardant) and 0.5 phr of tetrabromobisphenol A—traditional, highly effective flame retardant components—enabling it to achieve a UL 94 V-0 flame retardancy rating at a thin-wall thickness of 3.0 mm, making it suitable for use in electrical enclosures that require high flame retardancy.
High transparency. Compared to conventional flame-retardant polycarbonate materials, the greatest advantage of Lexan 920A-116 FR PC resin is its transparency: at a thickness of 2.54 mm, it has a light transmission of 85% and haze of only 1%, making it suitable for applications with high aesthetic requirements.
Good processability. Lexan 920A-116 PC resin has a melt flow rate of 14.5 g/10 min at 300°C and 1.2 kgf, which is a moderate flow rate suitable for conventional injection molding equipment. Additionally, this material contains a release agent, which facilitates product processing.

Why choose Baiyou as Sabic Lexan 920A-116 FR PC supplier?

Leading flame retardant polycarbonate supplier (PC material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Sabic Lexan 920A-116 PC
Product information
Manufacturer		Saudi Basic Industry Corporation
Other Certificates		MSDS
Part Marking Code		>PC material<
Color		Transparent polycarbonate
Material Shape		PC Pellets
Process		Injection molding
Features		·UL 94 V-0 flame retardant ·Transparent
Additives		Mold release
Physical properties	Standard	Value	Unit
Density	ASTM D792	1217	g/cm³
Melt flow rate, MVR at 300℃/1.2 kgf	ASTM D1238	14.5	g/10min
Mold shrinkage, flow, 3.2 mm	SABIC METHOD	0.5-0.7	%
Moisture absorption 23℃ 50% RH	ISO 62	0.15	%
Water absorption 23℃ saturated	ISO 62	0.35	%
Water absorption 23℃ 24 hrs	ISO 62	0.15	%
Specific volume	ASTM D792	0.83	cm³/g
Specific gravity	ASTM D792	1.21
Mechanical behavior	Standard	Value	Unit
Tensile stress, yield, Type Ⅰ, 50 mm/min	ASTM D638	62	MPa
Tensile stress, break,Type Ⅰ, 50 mm/min	ASTM D638	55	MPa
Tensile strain, yield, Type Ⅰ, 50 mm/min	ASTM D638	7	%
Tensile strain, break, Type Ⅰ, 50 mm/min	ASTM D638	90	%
Flexural stress,yield, 1.3 mm/min, 50 mm span	ASTM D790	91	MPa
Flexural modulus, 1.3 mm/min, 50 mm span	ASTM D790	2240	MPa
Hardness, rockwell M	ASTM D785	70
Hardness, rockwell R	ASTM D785	118
Taber abrasion, CS-17, 1 kg	ASTM D1044	10	mg/1000cy
Impact	Standard	Value	Unit
Izod impact, unnotched 23℃	ASTM D4812	3204	J/m
Izod impact, notched 23℃	ASTM D256	640	J/m
Tensile impact strength, Type S	ASTM D1822	525	J/m
Falling dart impact (D 3029), 23 ℃	ASTM D 2039	169	J/m
Thermal	Standard	Value	Unit
Vicat Softening Temperature, rate B/50	ASTM D1525	151	°C
Thermal conductivity	ASTM C177	0.19	W/m·℃
CTE, -40℃ to 95℃ flow	ASTM E831	6.84E-05	1/℃
HDT, 0.45 MPa, 6.4 mm, unannealed	ASTM D648	137	℃
HDT, 1.8 MPa, 6.4 mm, unannealed	ASTM D648	132	℃
Relative Temp index .Elec	UL746B	130	℃
Relative Temp index. Mech w / impact	UL746B	120	℃
Relative Temp index. Mech w / o impact	UL746B	130	℃
Electrical	Standard	Value	Unit
Volume resistivity	ASTM D257	>1.E+17	Ω.cm
Dielectrics strength, in air, 3.2mm	ASTM D149	16.7	kV/mm
Relative permittivity,50 / 60 Hz	ASTM D150	3.01
Relative permittivity,1 MHz	ASTM D150	2.96
Dissipation factor, 50 / 60 Hz	ASTM D150	0.0009
Dissipation factor, 1 MHz	ASTM D150	0.01
Arc resistance, tungsten {PLC}	ASTM D495	7
Hot wire ignition {PLC}	UL 746A	2
High voltage Arc track rate {PLC}	UL 746A	3
High Ampere Arc ign, surface {PLC}	UL 746A	3
Comparative tracking index {PLC}	UL 746A	2
Flame retardant	Standard	Value	Unit
UL recognized, 94V-2 Flame Class Rating	UL 94	1.5	mm
UL recognized, 94V-0 Flame Class Rating 2nd value	UL 94	3.0	mm
Optical	Standard	Value	Unit
Light transmission, 2.54mm	ASTM D1003	85	%
Haze, 2.54mm	ASTM D1003	1	%
Refractive index	ISO 489	1.586
Injection molding guidance	Standard	Value	Unit
Drying temperature		120	℃
Drying time		3-4	hrs
Maximum moisture content		0.02	%
Melt temperature		290-310	℃
Nozzle temperature		280-305	℃
Front - Zone 3 temperature		290-310	℃
Middle - Zone 2 temperature		275-300	℃
Rear- Zone 1 temperature		265-290	℃
Back pressure		0.3-0.7	MPa
Mold temperature		70-95	℃
Screw speed		40-70	rpm
Shot to cylinder size		40-60	%
Vent depth		0.025-0.076	mm