Mitsubishi lupilon s-3000ur polycarbonate

Mitsubishi Lupilon S-3000UR PC

Material attribute: ·UV resistance ·Mold release improved

Package: 25 KG/Bag

Process: Injection molding

Get Quotation

Mitsubishi Lupilon S-3000UR PC Description

Lupilon S-3000UR is a medium flow polycarbonate (PC resin) manufactured by Mitsubishi Engineering Plastics Corporation. It contains UV stabilizers and can be used to produce outdoor products.

The Mitsubishi Lupilon S-3000UR is manufactured in several locations—China, Thailand, and Japan. If you have specific requirements regarding the country of origin, please contact us.👉+86 15837933829.

As shown in the figure on the left, Mitsubishi Lupilon S-3000UR clear polycarbonate resin comes in several forms: the top one is transparent with blue background, the bottom left one is transparent with white tint, and the bottom right one is transparent with gray tint; all are roughly cylindrical in shape.

Mitsubishi Lupilon S-3000UR PC Advantage

UV stabilized PC, Mitsubishi Lupilon S-3000UR contains UV stabilizers that effectively prevent yellowing and performance degradation caused by sunlight exposure, making it suitable for the production of outdoor products.
Good processability. Lupilon S-3000UR PC resin has a melt volume rate (MVR) of 15 g/10 min under test conditions of 300°C and 1.2 kg, indicating moderate flow rate. It effectively improves demolding performance and is suitable for the vast majority of injection molding machines.

Why choose Baiyou as Mitsubishi Lupilon S-3000UR PC supplier?

Leading polycarbonate resin supplier (PC material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Mitsubishi Lupilon S-3000UR PC
Product information
Manufacturer		Mitsubishi engineering plastic company
Other Certificates		MSDS
Part Marking Code		>PC material<
Color		Transparent polycarbonate
Material Shape		PC Pellets
Process		Injection molding
Features		·Medium liquidity ·UV stabilized
Additives		·UV stabilizer
Physical properties	Standard	Value	Unit
Density	ISO 1183	1200	kg/m³
Melt volume rate, MVR at 300℃/1.2kg	ISO 1133	14	cm³/10min
Melt mass-flow rate, MFR at 300℃/1.2kg	ISO 1133	15	cm³/10min
Mold shrinkage, flow	Mitsubishi METHOD	0.5-0.7	%
Mold shrinkage, xflow	Mitsubishi METHOD	0.5-0.7	%
Water absorption 24 hr, 23℃	ISO 62	0.24	%
Mechanical behavior	Standard	Value	Unit
Tensile modulus	ISO 527	2400	MPa
Tensile stress, yield	ISO 527	62	MPa
Tensile strain, yield	ISO 527	6.7	%
Tensile strain, break	ISO 527	120	%
Flexural stress	ISO 178	93	MPa
Flexural modulus	ISO 178	2300	MPa
Impact	Standard	Value	Unit
Charpy notched impact strength, 23℃	ISO 179	67	kJ/㎡
Charpy unnotched impact strength, 23℃	ISO 179	NO break	kJ/㎡
Thermal	Standard	Value	Unit
Deflection Temperature under load 0.45 MPa, unannealed	ISO 75	139	°C
Deflection Temperature under load 1.8 MPa, unannealed	ISO 75	139	°C
CLTE, xflow	ISO 11359-2	6.6E-5	cm/cm/℃
CLTE, flow	ISO 11359-2	6.5E-5	cm/cm/℃
Electrical	Standard	Value	Unit
Volume resistivity	IEC 60093	3.0E+15	ohms·cm
Surface resistivity	IEC 60093	6.0E+15	ohms
Dielectrics constant, 1 MHz	IEC 60250	3.1	kV/mm
Dielectrics constant, 100 MHz	IEC 60250	3.1	kV/mm
Electric strength, 1.0 mm	IEC 60243-1	31	kV/mm
Electric strength, 3.0 mm	IEC 60243-1	18	kV/mm
Dissipation factor, 100 MHz	IEC 60250	6.0E-4
Dissipation factor, 1 MHz	IEC 60250	9.0E-4
Comparative tracking index (CTI)	UL 746A	PLC 2
Injection molding guidance	Standard	Value	Unit
Drying temperature		120	℃
Drying time		4-8	hrs
Nozzle temperature		270-300	℃
Front - Zone 3 temperature		270-300	℃
Middle - Zone 2 temperature		270-300	℃
Rear- Zone 2 temperature		270-280	℃
Mold temperature		70-100	℃