SABIC Cycoloy XCY620S heat resistant polycarbonate

SABIC Cycoloy XCY620S PC+ABS

Material attribution: ·Heat resistant ·Hydrolysis resistant

Package: 25KG/Bag

Process: Injection molding

Get Quotation

SABIC Cycoloy XCY620S PC+ABS pellet Description

Cycoloy XCY620S is a hydrolysis-resistant polycarbonate and acrylonitrile-butadiene-styrene blend produced by Saudi Basic Industry Corporation. Also known as"PC/ABS"or"PC+ABS,"it boasts excellent high-temperature resistance, a melt index of 23 (at 260°C, 5kg), and a high flow rate, making it easy to inject.

SABIC Cycoloy XCY620S PC+ABS pellet Advantage

Excellent hydrolysis resistance. Sabic Cycoloy XCY620S PC alloy material has good hydrolysis resistance. Even in high temperature and high humidity environments and outdoor application scenarios, it can still maintain good mechanical properties. It can be used in the production of automobile engine compartments, lampshade shells, etc.
Withgood high temperature resistance, Sabic XCY620S PC/ABS mixed plastic alloy material has a heat deformation temperature of 128°C at a test thickness of 3.2mm under a test environment of 0.45MPa. It can be used in normal temperature environments.

Why choose Baiyou as SABIC Cycoloy XCY620S PC+ABS pellets supplier?

Leading polycarbonate and Acrylonitrile-butadiene-styrene blend resin pellets supplier (PC/ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Product information
SABIC XCY620S PC+ABS
Manufacturer		Saudi basic industry corporation
Part Marking Code		>PC/ABS material<
Color		·Nactural color ·Black
Material Shape		·PC+ABS pellets
Process		Injection molding
Material Attribute		·Hydrolysis stabilized grade
Physical properties	Standard	Value	Unit
Density	ASTM D792	1.14	g/cm³
Density	ISO 1183	1.14	g/cm³
Shrinkage flow 3.2mm	Internal method	0.5~0.7	%
Shrinkage xflow 3.2mm	Internal method	0.5~0.7	%
Water absorption 23℃ 24hr	ISO 62	0.3	%
Melt index 260℃ 5kg	ASTM D1238	23	g/10min
Mechanical behavior	Standard	Value	Unit
Tensile strength yield 5mm/min Type Ⅰ	ASTM D638	60	MPa
Elongation break 5mm/min Type Ⅰ	ASTM D638	100	%
Flexural strength yield 1.3mm/min	ASTM D790	86	MPa
Flexural modulus 1.3mm/min	ASTM D790	2300	MPa
Izod notch impact 23℃	ASTM D256	680	J/m
Charpy notch impact 23℃ 1eA	ISO 179	60	kJ/㎡
Charpy notch impact -30℃ 4.00mm 1eA	ISO 179	45	kJ/㎡
Instrumented impact 23℃ total energy	ASTM D3763	55	J
Instrumented impact -30℃ total energy	ASTM D3763	65	J
Thermal	Standard	Value	Unit
HDT unannealed 0.45MPa 3.2mm	ASTM D648	128	℃
HDT unannealed 1.8MPa 3.2mm	ASTM D648	108	℃
Vicat softening temperature 50℃/hr 50N	ASTM D1525	129	℃
Vicat softening temperature 120℃/hr 50N	ISO 306	130	℃
CLE flow -40~40℃	ASTM E831	7E-5	cm/cm/℃
CLE xflow -40~40℃	ASTM E831	7E-5	cm/cm/℃
Electrical properties	Standard	Value	Unit
Volume resistivity	IEC 60093	1E+16	Ω·cm
Surface resistivity	IEC 60093	1E+16	Ω
Dielectric strength 0.80mm in oil	IEC 60243	39	KV/mm
Dielectric strength 1.6mm in oil	IEC 60243	25	KV/mm
Dielectric strength 3.2mm in oil	IEC 60243	17	KV/mm
Injection molding	Standard	Value	Unit
Dry temperature		95~105	℃
Dry time		2~4	hr
Water content control		≤0.02	%
Zone 1 temperature		230~260	℃
Zone 2 temperature		250~290	℃
Zone3 temperature		250~290	℃
Nozzle temperature		240~280	℃
Cylinder temperature		60~80	℃
Melt temperature		260~290	℃
Mould temperature		60~90	℃

⚠️The technical data sheet (TDS) of Sabic cycoloy XCY620S polycarbonate and Acrylonitrile-butadiene-styrene blend resin pellets ( PC/ABS or PC+ABS material) from Saudi basic industry, if there are differences, please refer to the official website of Sabic.