ChiMei Polylac PA-757K ABS

Application: Copier housing

Density: 1.04 g/cm³

Melt index: 1.8 g/10 min

Get Quotation

CHIMEI Polylac PA-757K ABS pellet Description

Polylac PA-757K is a acrylonitrile-butadiene-styrene resin pellets (high gloss ABS material) produced by Zhenjiang Chimei Company. It has a melt index of 1.8 and is suitable for injection molding, is often used in the production of office equipment housings and home appliance housings.

As shown in the figure on the left, Chimei ABS PA 757K is a milky white, high-gloss plastic pellet. Compared to ABS produced by continuous mass polymerization, it has a slightly yellowish tint and is not pure white.

⚠️Chimei 757K and Chimei 757 ABS material have no difference in performance, formula and raw material, but the place of production is different."K"represents the production factory in Zhenjiang, China, and they can be used replaced.

ChiMei Polylac PA-757K ABS pellet Advantage

Good appearance properties. Products made of Chimei PA-757K ABS have higher gloss than other ABS materials of the same brand, and are suitable for home appliance housings, daily necessities, etc. that have high requirements for external appearance properties.
Good impact resistance. The Izod notch impact of Chimei PA757K ABS material is 18kg-cm/cm at 23℃ 6.4mm test environment. Its good impact resistance makes it suitable for office equipment housing manufacturing.
Good visual properties. Chimei PA 757K offers excellent gloss and can be used in plastic electroplating processes. The finished products are comparable to LG HI-121H and INEOS Terluran GP-22 ABS, but are more affordable and can serve as direct substitutes for these materials.

Why choose Baiyou as CHIMEI Polylac PA-757K ABS pellets supplier?

Leading high gloss Acrylonitrile-butadiene-styrene resin pellets supplier (ABS material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Zhenjiang ChiMei POLYAC PA-757K ABS pellets
Product information
Manufacturer		Zhenjiang ChiMei CO.,LTD
Part Marking Code		>ABS material<
Color		Natural Color
Material Shape		ABS Pellets
Process		Injection molding
Flame retardant		HB
Application		·Copier housing ·General purpose
Specification		UL
Features		·High gloss ·High stiffness ·Medium impact ·General purpose grade
Physical properties	Standard	Value	Unit
Density 23 ℃	ISO 1183	1.04	g/cm³
Melt Index 200℃ 5kg	ASTM D1238	1.8	g/10min
Melt Index 200℃ 10kg	ISO 1133	18	cm³/10min
Hardness	Standard	Value	Unit
Rockwell Hardness R(Scale)	ASTM D785	116
Mechanical behavior	Standard	Value	Unit
Tensile Strength 50mm/min	ISO 527	46	MPa
Tensile Strength 6mm/min 3.2mm	ASTM D638	480	kg/cm³
Elongation 50 mm/min	ISO 527	20	%
Elongation 6 mm/min, 3.2mm	ASTM D638	20	%
Flexural Strength 2.0mm/min	ISO 178	69	MPa
Flexural Strength 2.8mm/min 6.4mm	ASTM D790	790	kg/c㎡
Flexural modulus 2.0mm/min	ISO 178	2.4	GPa
Flexural modulus 2.8mm/min 6.4mm	ASTM D638	27000	kg/c㎡
Izod Notch Impact 23℃ 4.0mm	ISO 180	18	kJ/㎡
Izod Notch Impact 23℃ 6.4mm	ASTM D256	18	kg-cm/cm
Izod Notch Impact 23℃ 3.2mm	ASTM D256	20	kg-cm/cm
Charpy notch impact 23℃ 4.0 mm	ISO 179	20	kJ/㎡
Thermal	Standard	Value	Unit
HDT Annealed 1.8MPa	ISO 75	98	°C
HDT unannealed 1.8MPa	ISO 75	83	°C
HDT annealed 120℃/hr 6.4 mm annealed at 85 ℃ for 8 hours	ASTM D648	99	°C
HDT unannealed 120℃/hr 6.4 mm	ASTM D648	88	°C
Vicat softening temperature 50℃ /hr 10 N	ISO 306	103	°C
Vicat softening temperature 50℃ /hr 3.2 mm	ASTM D1525	105	°C
Flammability	Standard	Value	Unit
Flame rating all color 1.5 mm	UL 94	HB
Flame rating all color 3.0 mm	UL 94	HB