Teijin Panlite L-1250Y PC

Application：General purpose

Density: 1.2g / m³

Melt index: 8cm³ / 10min (300℃ 1.2kg)

Get Quotation

Teijin Panlite L-1250Y PC Description

Panlite L-1250Y is a general purpose polycarbonate (PC material) produced by Teijin Chemicals Co., Ltd. It has medium viscosity and good foaming properties, can be processed by injection molding and extrusion molding and has a wide range of applications.

Teijin L-1250Y Panlite PC Advantage

Highly transparent polycarbonate material, Teijin Panlite L-1250Y is a highly transparent PC pellet with better transparency, transmittance, and refractive index than its competitors, used for applications that require a high level of appearance.
Excellent processing performance. Panlite L-1250Y PC has a melt index of 8 cm³/10 min at 300°C (1.2 kg). This high melt index is suitable for the production of complex and precise parts. L-1250Y polycarbonate also contains a release agent, which reduces material residue in the mold and improves production efficiency.

Why choose Baiyou as Teijin Panlite L-1250Y PC pellets supplier?

Leading Polycarbonate resin pellets supplier (PC material) , 20+ years of experience in plastic product manufacturing and chemical raw material import and export
Fastest Arrival, with warehouses in multiple ports
1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
Free Samples for production testing
Wholesale price, even a piece of goods is based on the wholesale price

Key Attributes

Teijin Panlite L-1250Y PC
Product information
Manufacturer		Teijin chemical LTD.
Part Marking Code		>PC material<
Color		Transparent
Material Shape		PC pellets
Process		·Injection molding ·Extrusion molding
Viscosity		Medium viscosity
Flame retardant		HB V-2
specification		·RoHS ·UL ·UL-746C F2
Features		·Transparency ·Good mould release
Additives		Mold release
Application		General purpose
Physical property	Standard	Value	Unit
Density	ISO 1183	1.2	g/cm³
Shrinkage xFlow 4.0mm	Internal method	0.5~0.7	%
Water absorption 23℃ 1.2kg	ISO 62	0.20	%
Melt Index 300°C 1.2kg	ISO 1133	8	cm³/10 min
Mechanical behavior	Standard	Value	Unit
Tensile Modulus	ISO 527	2400	MPa
Tensile Strength Yield	ISO 527	61.0	MPa
Elongation yield	ISO 527	6.0	%
Elongation break	ISO 527	50	%
Flexural Strength 2.0mm/min	ISO 178	91	Mpa
Flexural modulus 2.0mm/min	ISO 178	2300	Mpa
Charpy Notch Impact	ISO 179	76	kJ/㎡
Charpy Un-notch Impact	ISO 179	NB	kJ/㎡
Optical	Standard	Value	Unit
Transmittance	ASTM D1003	88	%
Refractive	ASTM D542	1.585
Thermal	Standard	Value	Unit
Heat deflection temperature (HDT) unannealed 0.45Mpa	ISO 75	142	℃
Heat deflection temperature (HDT) unannealed 1.8 Mpa	ISO 75	129	℃
Vicat softending temperature 50℃/hr 50N	ISO 306	149	℃
CLE Flow	ISO 11359	7E-5	cm/cm/℃
CLE xFlow	ISO 11359	7E-5	cm/cm/℃
Flammability	Standard	Value	Unit
Flame Rating All color 1.5mm	UL94	HB
Flame Rating All color 3.0mm	UL94	HB

⚠️The technical data sheet of Teijin Panlite L-1250Y polycarbonate, from Teijin chemical, if there are differences, please refer to the official website of Teijin chemical.