Celanese Zytel MT409AHS heat resistant PA 66

Celanese Zytel MT409AHS NC010 PA 66

Material properties: Heat stabilized ; Impact modified

Package: 25KG/Bag

Process: Injection molding ; Extrusion molding
Get Quotation

 Celanese Zytel MT409AHS NC010 PA 66 Description 

Zytel MT409AHS NC010 is high temperature resistant polyamide 66 resin pellet produced by Celanese Polymers Corporation. It is also known as"PA 66 material"or"nylon 66 material", has good high temperature resistance, high impact resistance and appearance. MT409AHS PA 66 is often used in the production of automotive parts.

zytel mt409ahs high temperature nylon

Zytel MT409AHS NC010 natural-colored nylon, as shown in the figure on the left, is a cylindrical, off-white granule. Other standard colors include Zytel MT409AHS BK010—an opaque black.

If you need other colors or custom colors, please contact us.👉+86 15837933829

Celanese Zytel MT409AHS NC010 PA 66 Advantage

  • Better heat aging resistance. As shown in Table 1 below, compared with Zytel ST801 NC010, which is also a toughened nylon, Zytel MT409AHS NC010 PA 6,6 continues to exhibit excellent mechanical strength and electrical properties even under long term high temperature aging conditions, making it an excellent choice for high temperature nylon materials.
Zytel MT409AHS NC010 Zytel ST801 NC010
RTI, electrical, 0.75 mm130125℃
RTI, impact, 0.75 mm6575℃
RTI, strength, 0.75 mm9585℃
Table 1. Comparison of Zytel MT409AHS and Zytel ST801 in Terms of Relative Thermal Index (RTI)
  • Medium toughness reinforced, As shown in Table 2, compared with the more commonly used unreinforced Zytel 101L NC010 nylon, Zytel PA66 MT409AHS NC010 offers improved toughness and is suitable for automotive tubing fittings, clips, and connectors​​​​
Zytel MT409AHS NC010 Zytel 101L NC010
Izod notched impact strength, 23℃
185.5kJ/㎡
Izod notched impact strength, -30℃
155.5kJ/㎡
Charpy notched impact strength, 23℃
215.5kJ/㎡
Charpy notched impact strength, -30℃
134.5kJ/㎡
Nominal strain at break2525%
Tensile strain at yield, 50 mm/min54.5%
Table 2. Comparison of Zytel MT409AHS and Zytel 101l in Flexibility
  • Automotive applications Nylon. Zytel MT409AHS meets the certification requirements for PA 66 materials set by General Motors, Ford, the Volkswagen Group, Mercedes-Benz, and Stellantis-Chrysler, and can be used directly in automotive applications.

Why choose Baiyou as Celanese Zytel MT409AHS NC010 PA 66 supplier?

  • Leadinghigh temperature Nylon resin supplie, 20+ years of experience in plastic product manufacturing and chemical raw material import and export
  • Fastest Arrival, with warehouses in multiple ports
  • 1,000+ types of resins are available, and we have cooperated with large petrochemical groups for 30+ years
  • Free Samples for production testing
  • Wholesale price, even a piece of goods is based on the wholesale price
 Key Attributes 
Celanese Zytel MT409AHS NC010 PA 66
Product information
Manufacturer
Celanese Corporation
Part Marking Code
>PA66 material<
Color·Natural color ·Black
Material Shape
·PA66 pellets 
Process·Injection molding ·Extrusion molding
Flame retardant·HB
Material Attribute
·Impact modified ·Heat stabilized grade Nylon 
Specification·ASTM D4066 PA0161 ·ASTM D6679 PA0161 ·UL ·UL-746 F2 
Features
·Good appearance ·Good knit line strength ·High stiffness ·Good processability
Automotive specifications
·GM GMP.PA66.079 ·GM GMP.PA66.015 ·GM GMP.PA66.063 ·GM GMW16447P-PA66-T2 ·GM GMW16558P-PA66-T1
·CHRYSLER MS-DB-41 CPN2055 ·FORD WSK-M4D706-A  ·FORD WSS-M4D706-B1 ·VW Group VW 50127 PA66-2
·VW Group VW 50127 PA66-2-A ·Mercedes-Benz DBL5410.01 PA66-I ·Stellantis MS.50017 / PA66-EPDM.1600F.20I.HS
Additives·Heat stabilized ·Impact modifier ·Mold release
Physical propertiesStandardValueUnit
Density
ISO 1183
1.11
g/cm³
Shrinkage xFlowISO 2941.7%
Shrinkage FlowISO 2941.5%
Water absorption 23℃ 24hrISO 621.3%
Water absorption 23℃ saturation 2.0mm
ISO 627.2%
Melt density0.930g/cm³
HardnessStandardDryWetUnit
Ball Pressure Hardness H132/30ISO 203912560MPa
Mechanical behavior
Standard
DryWet
Unit
Tensile modulus
ISO 52724001100
MPa
Tensile strengthISO 52761.043.0MPa
Elongation yieldISO 5275.028%
Elongation breakISO 5272550%
Elongation flow yieldISO 5274.4%
Poission Ratio0.380.45
Flexural strengthISO 17875.053.0MPa
Flexural modulusISO 17822001000MPa
Izod notch impact -40℃ISO 1801311kJ/㎡
Izod notch impact -30℃ISO 1801515kJ/㎡
Izod notch impact 23℃ISO 1801829kJ/㎡
Charpy notch impact -40℃ISO 17913kJ/㎡
Charpy notch impact -30℃ISO 1791313kJ/㎡
Charpy notch impact 23℃ISO 1792140kJ/㎡
Charpy un-notch impact -30℃ISO 179NBNBkJ/㎡
Charpy un-notch impact 23℃ISO 179NBNBkJ/㎡
Thermal
Standard
Value
Unit
HDT unannealed 0.45MPa
IEC 75205
℃
HDT unannealed 1.8MPaIEC 7566.0
℃
Melt temperature 10℃/minISO 11357262℃
Glass transition temperature 10℃/minISO 1135780℃
CLE Flow
ISO 113591E-4cm/cm/℃
CLE xFlowISO 113591.2E-4cm/cm/℃
Heat conductivity coefficient melt0.14W/(m·K)
Specific heat melt2730J/(kg·℃)
Electrical properties
Standard
DryWet
Unit
Volume resistivity
IEC 626311E+133E+10
Ω·cm
Surface resistivityIEC 62631-3-21E+13Ω
Dielectric strength 
IEC 602432322
KV/mm
Dielectric constant 1MHzIEC 62631-2-13.403.70
 
Dielectric constant 100HzIEC 62631-2-13.606.60
Dissipation factor 100HzIEC 62631-2-10.0050.18
Dissipation factor 1MHzIEC 62631-2-10.0120.044
CTIIEC 60112600V
Flammability
Standard
Value
Unit
Flame rating natural color / Black 0.8mm
UL94
HB
 
Flame rating natural color / Black 1.5mmUL94HB
Flame rating natural color / Black 3.0mmUL94HB
Limiting oxygen indexISO 458920%
Burning rate 1.0mmISO 379529mm/min
VDA properties
Standard
Value
Unit
Emission of organic compoundsVDA 27710.0μg/g
Fogging G-value condensateISO 64520.10mg
OdourVDA 2704.00
Injection molding
Standard
Value
Unit
Dry temperature80℃
Dry time2.0~4.0hr
Water content control≤0.20%
Melt temperature280~300℃
Melt temperature290℃
Mould temperature50~100℃
Holding pressure50.0~100MPa
Hold pressure time4.0s/mm
 Partners 
We have established long-term relationships with 80+ well-known  companies around the world
 Warehouse And Shipping 
20+ years' experience consultant with a supply chain of 1000+ plastic raw materials in China.
Quantity (tonnes)
1-100
100-300
>300
Lead time (days)
7-10
10-15
To be negotiated

References and Notes

  1. Celanese,"Zytel MT409AHS NC010 nylon resin technical data sheet", Celanese corporation, 15/06/2026